Huntsman IROGRAN® A 78 P 4766 TPU-Polyether
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 78 P 4766 TPU-Polyether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent resistance to hydrolysis and microbial attack. Suggested for injection molding and extrusion.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D995 |
| Melt Flow | 80 - 120 g/10 min | 80 - 120 g/10 min | Melt Volume Rate (cm³/10 min) |
| Melt Index of Compound | 110 g/10 min @Load 21.6 kg, Temperature 190 °C |
110 g/10 min @Load 47.6 lb, Temperature 374 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 82 | 82 | ASTM D2240 |
| Hardness, Shore D | 30 | 30 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | DIN 53504 |
| Elongation at Break | 910 % | 910 % | ASTM D412 |
| 100% Modulus | 0.00520 GPa | 0.754 ksi | DIN 53504 |
| 300% Modulus | 0.00800 GPa | 1.16 ksi | DIN 53504 |
| Rebound | 50 % | 50 % | Bayshore; ASTM D2632 |
| Tear Strength | 71.9 kN/m | 410 pli | ASTM D624 |
| Abrasion | 40 | 40 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 20 % @Temperature 23.0 °C, Time 252000 sec |
20 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 36 % @Temperature 70.0 °C, Time 86400 sec |
36 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 190 °C | 329 - 374 °F | Huntsman/TMA |
| Flammability, UL94 | V-0 | V-0 | Non-Halogen FR |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, at 50% RH (dis
- Karina E 18/35-FC-LMP Gray Color Concentrate for PVC
- SABIC Innovative Plastics ULTEM CRS5211R PEI (Asia Pacific)
- SABIC Innovative Plastics NORYL GTX GTX987 PPE+PA66
- A. Schulman FORMION™ FI 226 40% Glass Fiber Reinforced Ionomer / Nylon Alloy
- DuPont 20 Series DPE 20 Specialty Polyethylene Resin
- ConocoPhillips Conoco® El Mar® Ashless Heavy Duty Oil, SAE Viscosity Grade 30
- ExxonMobil Escorene™ FL 01418 Ethylene Vinyl Acetate Copolymer (European Grade)
- Abatron AboSeal 8104-14 Polysulfide, Thixotropic Sealant and Caulk
Copyright © lookpolymers.com All Rights Reserved