LATI Larpeek 50 PEEK

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced
Manufacturer LATI
Trade Name Larpeek
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larpeek 50 PEEK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyetheretherketone (PEEK). Unfilled. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
Linear Mold Shrinkage, Flow 0.0085 - 0.0125 cm/cm
0.0085 - 0.0125 in/in
Linear Mold Shrinkage, Transverse 0.0095 - 0.0135 cm/cm
0.0095 - 0.0135 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa

@Temperature 150 °C
 4350 psi

@Temperature 302 °F
50.0 MPa

@Temperature 120 °C
 7250 psi

@Temperature 248 °F
60.0 MPa

@Temperature 90.0 °C
 8700 psi

@Temperature 194 °F
75.0 MPa

@Temperature 60.0 °C
 10900 psi

@Temperature 140 °F
85.0 MPa

@Temperature 23.0 °C
 12300 psi

@Temperature 73.4 °F
Elongation at Break 30 %

@Temperature 23.0 °C
 30 %

@Temperature 73.4 °F
30 %

@Temperature 60.0 °C
 30 %

@Temperature 140 °F
30 %

@Temperature 90.0 °C
 30 %

@Temperature 194 °F
35 %

@Temperature 120 °C
 35 %

@Temperature 248 °F
45 %

@Temperature 150 °C
 45 %

@Temperature 302 °F
Elongation at Yield 5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
5.0 %

@Temperature 60.0 °C
 5.0 %

@Temperature 140 °F
5.0 %

@Temperature 90.0 °C
 5.0 %

@Temperature 194 °F
6.0 %

@Temperature 120 °C
 6.0 %

@Temperature 248 °F
8.0 %

@Temperature 150 °C
 8.0 %

@Temperature 302 °F
Tensile Modulus 3.00 GPa

@Temperature 150 °C
 435 ksi

@Temperature 302 °F
3.40 GPa

@Temperature 120 °C
 493 ksi

@Temperature 248 °F
3.45 GPa

@Temperature 90.0 °C
 500 ksi

@Temperature 194 °F
3.50 GPa

@Temperature 23.0 °C
 508 ksi

@Temperature 73.4 °F
3.50 GPa

@Temperature 60.0 °C
 508 ksi

@Temperature 140 °F
Charpy Impact Unnotched NB
NB
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Coefficient of Friction, Dynamic 0.26
0.26
Coefficient of Friction, Static 0.32
0.32
K (wear) Factor 15.0 x 10-8 mm³/N-M
7.45 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 200 °C
392 °F
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Vicat Softening Point >= 300 °C

@Load 5.00 kg
 >= 572 °F

@Load 11.0 lb
Flammability, UL94 V-1

@Thickness 0.750 mm
 V-1

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Glow Wire Test 875 °C

@Thickness 1.00 mm
 1610 °F

@Thickness 0.0394 in
 GWIT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Processing Properties Metric English Comments
Melt Temperature 360 - 390 °C
680 - 734 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 - 150 °C

@Time 10800 sec
 248 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa