Honeywell Capran® Oxyshield™ OEB (1.0 mil) Monoaxially Oriented, Co-Extruded Nylon6/EVOH/Nylon 6 Clear Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | Honeywell |
| Trade Name | Capran® Oxyshield™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Oxyshield™ OEB (1.0 mil) Monoaxially Oriented, Co-Extruded Nylon6/EVOH/Nylon 6 Clear Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Oxyshieldâ„¢ Oriented Extra Barrier is a 1.00 (25micron) monoaxially oriented, co-extruded nylon 6/EVOH/nylon 6 clear film having excellent gas barrier through a broad range of relative humidity. The film provides high strength, good chemical resistance, and excellent flavor and aroma barrier for food packaging. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Water Vapor Transmission | 116 g/m²/day | 7.47 g/100 in²/day | 100°F (37.8°C) / 100%RH; ASTM F1249 |
| Oxygen Transmission Rate | 0.470 cc/m²/day | 0.0303 cc/100 in²/day | 73°F (23°C) / 65%RH; ASTM D3985 |
| Thickness | 25.4 microns | 1.00 mil | |
| Surface Tension | >= 56 dynes/cm | >= 56 dynes/cm | treated side; ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, TD | 68.9 - 82.7 MPa | 10000 - 12000 psi | ASTM D882 |
| Film Elongation at Break, MD | 55 - 80 % | 55 - 80 % | ASTM D882 |
| Film Elongation at Break, TD | 180 - 425 % | 180 - 425 % | ASTM D882 |
| Secant Modulus, MD | 3.275 - 4.689 GPa | 475.0 - 680.1 ksi | ASTM D882 |
| Secant Modulus, TD | 2.586 - 3.448 GPa | 375.1 - 500.1 ksi | ASTM D882 |
| Coefficient of Friction | 0.25 - 0.57 | 0.25 - 0.57 | film to stainless steel; ASTM D1894 |
| 0.66 - 2.0 | 0.66 - 2.0 | film to film; ASTM D1894 | |
| Tear Strength Test | 925 - 1450 | 925 - 1450 | graves tear TD, grams/mil; ASTM D1004 |
| 1000 - 14000 | 1000 - 14000 | graves tear MD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 200 - 290 MPa | 29000 - 42000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 48.3 - 96.5 MPa | 7000 - 14000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | <= 11 % | <= 11 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | <= 2.5 % | <= 2.5 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 6.0 % | <= 6.0 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9970H TPE, ABS/PC Overmold
- Kolon DIAMAT® IM
- Lubriplate H0-2A Petroleum-Based Heavy-Duty Hydraulic Oil
- Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld
- MTI ThermoStran® PA66-60G Long Glass Fiber Compound
- Schott GM31685 Dental Glass
- Solvay Specialty Polymers Diofan® A 299 Polyvinylidene Chloride (PVDC)
- Eurostar Starflam AFR450X1 PA66, 25% Glass Filled, Injection Molded
- Aclo Accutech Polypropylene Homopolymer HP0334C20L1 Calcium Reinforced
- CENTROPLAST CENTROTRON GF 15 Polyphenylene sulfide 15% glass fiber
Copyright © lookpolymers.com All Rights Reserved