- Techmer ES HiFill® PP LGF50 CC NAT 12mm 50% Glass Filled
Techmer ES HiFill® PP LGF50 CC NAT 12mm 50% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 50% Glass Fiber Filler |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PP LGF50 CC NAT 12mm 50% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Long Glass Fiber, 50% Filler by WeightFeatures: Chemically CoupledInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 128 MPa | 18500 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 2.03 J/cm @Thickness 3.17 mm |
3.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 7.47 J/cm @Thickness 3.17 mm |
14.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.6 µm/m-°C | 12.0 µin/in-°F | ASTM D696 |
| Melting Point | 163 °C | 325 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 310 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.1 kV/mm | 510 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- LNP NORYL® EXCP0111 PPS + Polyphenylene Ether, 42% Glass / Mineral Reinforcement (discontinued **)
- PolyOne Edgetek® LCP-15GF/000 Liquid Crystal Polymer - 15% Fiber Glass (discontinued **)
- Huntsman Araldite GT 6243 Bisphenol A Epoxy Solid Resin
- Lubrizol Advanced Materials PEARLCOAT® 165K Thermoplastic Polyurethane Elastomer
- Stir SpA Giesse EPM/78 (PVC)
- Toyobo GLAMIDE® T-602G30 MXD66
- A. Schulman POLYFORT™ FPP 1477 Mineral Filled, General-Purpose Polypropylene
- Daikin POLYFLON MG-1040F PTFE 20% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow
- A. Schulman POLYBATCH™ Blue 40460/4 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved