- Lucent Polymers PC/ABS-1211P Polycarbonate+ABS, Impact Modified, Platable, Injection Grade
Lucent Polymers PC/ABS-1211P Polycarbonate+ABS, Impact Modified, Platable, Injection Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers PC/ABS-1211P Polycarbonate+ABS, Impact Modified, Platable, Injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 260 °C |
11 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.03 MPa | 7401 psi | ASTM D638 |
| Elongation at Break | >= 140 % | >= 140 % | ASTM D638 |
| Flexural Strength | 68.97 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 2.069 GPa | 300.1 ksi | ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
6.00 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 |
| 6.41 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
12.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.89 °C | 210.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Ineos Styrenics Avantra® 2710 High Impact Styrenic Polymer (Global)
- Lanxess Durethan® DP 1852/30 000000 Nylon 6, 30% Glass Fiber
- Solvay Specialty Polymers Polymist® F284 Polytetrafluoroethylene (PTFE)
- Cosmic Plastics 6130F Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Polyram RamShine PV701 ABS, UV Stabilized
- ExxonMobil LLDPE LL 1004YB Film Linear Low Density Polyethylene Resin (European Grade)
- Braskem FG31D LLDPE Blown Film Extrusion Polyethylene Copolymer
- REXtac Rextac® RT 3585 Amorphous Polyalphaolefin (APAO)
Copyright © lookpolymers.com All Rights Reserved