Honeywell Aegisâ„¢ H135QP Nylon 6 Extrusion Grade Homopolymer Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | Honeywell |
| Trade Name | Aegis™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Aegisâ„¢ H135QP Nylon 6 Extrusion Grade Homopolymer Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Aegis H135QP is a lubricated high viscosity, N6, film extrusion grade homopolymer for cast or blown film. It conforms to FDA requirements including, 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermo-forming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance.Applications:Processed MeatFresh Red MeatPoultryFishCheeseDried FoodChilled Fruit JuicesInformation provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D1505 |
| Water Absorption | 0.80 % | 0.80 % | Extractable Content |
| 1.6 % | 1.6 % | in 24 hours | |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | at 50% RH |
| Water Absorption at Saturation | 9.5 % | 9.5 % | |
| Oxygen Transmission Rate | 40.3 cc/m²/day | 2.60 cc/100 in²/day | |
| Nitrogen Transmission | 14.0 cc-mm/m²-24hr-atm | 35.6 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Carbon Dioxide Transmission | 72.8 cc-mm/m²-24hr-atm | 185 cc-mil/100 in²-24hr-atm | cc/m²/day, No thickness given |
| Viscosity Measurement | 135 | 135 | FAV; ASTM D789 |
| Maximum Moisture Content | 0.080 | 0.080 | |
| Melt Flow | 1.2 g/10 min @Load 1.00 kg, Temperature 235 °C |
1.2 g/10 min @Load 2.20 lb, Temperature 455 °F |
ASTM D1238 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Cast Film |
| 246 - 254 °C | 475 - 489 °F | Tubular (Blown) Film | |
| Adapter Temperature | 260 °C | 500 °F | Tubular (Blown) Film |
| 260 - 266 °C | 500 - 511 °F | Cast Film | |
| Die Temperature | 254 °C | 490 °F | Tubular (Blown) Film |
| 260 °C | 500 °F | Cast Film | |
| Melt Temperature | 254 - 260 °C | 489 - 500 °F | Tubular (Blown) Film |
| 260 - 270 °C | 500 - 518 °F | Cast Film | |
| Moisture Content | 0.080 % | 0.080 % |
Users viewing this material also viewed the following:
- Nylene® Naxel™ PC10 Polycarbonate
- Ovation Polymers Nemcon™ E PK DP104 Polyetheretherketone, Carbon Fiber Reinforced
- Reade Advanced Materials Strontium Sulfate Powder (Celestite) (SrSO4)
- PolyOne Geon™ CPVC EC050 Polyvinyl Chloride, Chlorinated (CPVC)
- Okulen® 2000 PE-UHMW, OF
- Ravago Manufacturing Americas Enviramid™ N2340MHL BK Post Consumer Recycle Nylon 6, 40% Mineral Filled
- Abatron AboCast 8101-8/AboCure 8101-8 Epoxy (discontinued **)
- Industeel SUPRALSIM® 690 HLE Steel for Welded and Weight-Saving Structures
- Mo-Sci Corporation GL-0261 Ni Coated Borosilicate Glass Spheres
- Colorite Polymers 8000 General Purpose Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved