Daelim H&L Plavis G40 Aromatic Polyimide, 40% Graphite Filled, Direct Formed (Unverified Data**)
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Daelim H&L Plavis G40 Aromatic Polyimide, 40% Graphite Filled, Direct Formed
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Daelim H&L
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 66 - 70 | 66 - 70 | ASTM D785 |
| Tensile Strength, Ultimate | 35.7 MPa <br>@Temperature 260 °C |
5180 psi <br>@Temperature 500 °F |
ASTM D1708 |
| 65.4 MPa <br>@Temperature 23.0 °C |
9490 psi <br>@Temperature 73.4 °F |
ASTM D1708 | |
| Tensile Strength, Yield | 28.1 MPa <br>@Strain 1.00 % |
4080 psi <br>@Strain 1.00 % |
ASTM D95 |
| 98.36 MPa <br>@Strain 10.0 % |
14270 psi <br>@Strain 10.0 % |
ASTM D95 | |
| Elongation at Break | 3.4 % <br>@Temperature 260 °C |
3.4 % <br>@Temperature 500 °F |
ASTM D1708 |
| 5.5 % <br>@Temperature 23.0 °C |
5.5 % <br>@Temperature 73.4 °F |
ASTM D1708 | |
| Flexural Strength | 38.8 MPa <br>@Temperature 260 °C |
5630 psi <br>@Temperature 500 °F |
ASTM D790 |
| 75.9 MPa <br>@Temperature 23.0 °C |
11000 psi <br>@Temperature 73.4 °F |
ASTM D790 | |
| Flexural Modulus | 2.0638 GPa <br>@Temperature 260 °C |
299.33 ksi <br>@Temperature 500 °F |
ASTM D790 |
| 3.2966 GPa <br>@Temperature 23.0 °C |
478.13 ksi <br>@Temperature 73.4 °F |
ASTM D790 | |
| Compressive Modulus | 2.8351 GPa <br>@Temperature 23.0 °C |
411.20 ksi <br>@Temperature 73.4 °F |
ASTM D695 |
| Izod Impact, Notched (ISO) | 4.1202 kJ/m² | 1.9609 ft-lb/in² | ASTM D256 |
| Coefficient of Friction | 0.14 | 0.14 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 2.50 µm/m-°C <br>@Temperature 23.0 - 260 °C |
1.39 µin/in-°F <br>@Temperature 73.4 - 500 °F |
ASTM D696 |
| Decomposition Temperature | 616 °C | 1140 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 50% Weight Reduction Time (Minutes) | 240 |
Users viewing this material also viewed the following:
- Huntsman KRYSTALFLEX® PE 192 Polyurethane Optical Aliphatic Film
- IDI Composites C-103 Thermoset Polyester, Molding
- Global F-8000 High Density Polyethylene
- Materion Brush 1915â„¢ AT Temper Rod
- Universal Wire Works 19-9WMo (AMS 5782) Filler Metal
- Universal Wire Works Au-Pd-Ni (AMS 4784) Gold Brazing Filler Metal
- Hexcel® HexWeb® CR III 5/32-5052-.001 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Borealis Supersmooth™ LE0500 Crosslinkable Semiconductive Shielding Compound
- Crucible Steel CSM® 6 Tool Steel, AISI A6
- Arlon 912-10C16.4FR-P0 0.012" (0.305 mm) Self-Fusing Silicone Tape
Copyright © lookpolymers.com All Rights Reserved