- Hexcel® HexPly® EF01 Epoxy Curing System after 1031 2 1000 970 EF01 31% Cure Cycle
Hexcel® HexPly® EF01 Epoxy Curing System after 1031 2 1000 970 EF01 31% Cure Cycle
| Category | Polymer , Thermoset , Epoxy , Epoxy Cure Resin |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® EF01 Epoxy Curing System after 1031 2 1000 970 EF01 31% Cure Cycle.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 1050.7 MPa @Temperature 50.0 °C |
152390 psi @Temperature 122 °F |
Flexure Weft; 13 min @ 250°F; prEN 2563 |
| 1060.8 MPa @Temperature 50.0 °C |
153850 psi @Temperature 122 °F |
Flexure Weft; 15 min @ 250°F; prEN 2563 | |
| 1080.8 MPa @Temperature 50.0 °C |
156750 psi @Temperature 122 °F |
Flexure Weft; 10 min @ 250°F; prEN 2563 | |
| 1150.8 MPa @Temperature 22.8 °C |
166910 psi @Temperature 73.0 °F |
Flexure Weft; 10 min @ 250°F; prEN 2563 | |
| 1150.8 MPa @Temperature 22.8 °C |
166910 psi @Temperature 73.0 °F |
Flexure Weft; 15 min @ 250°F; prEN 2563 | |
| 1150.8 MPa @Temperature 22.8 °C |
166910 psi @Temperature 73.0 °F |
Flexure Weft; 13 min @ 250°F; prEN 2563 | |
| Flexural Modulus | 39.0 GPa @Temperature 22.8 °C |
5660 ksi @Temperature 73.0 °F |
Flexure Weft; 10 min @ 250°F; prEN 2563 |
| 39.0 GPa @Temperature 22.8 °C |
5660 ksi @Temperature 73.0 °F |
Flexure Weft; 15 min @ 250°F; prEN 2563 | |
| 39.0 GPa @Temperature 22.8 °C |
5660 ksi @Temperature 73.0 °F |
Flexure Weft; 13 min @ 250°F; prEN 2563 | |
| 39.0 GPa @Temperature 50.0 °C |
5660 ksi @Temperature 122 °F |
Flexure Weft; 15 min @ 250°F; prEN 2563 | |
| 40.1 GPa @Temperature 50.0 °C |
5810 ksi @Temperature 122 °F |
Flexure Weft; 10 min @ 250°F; prEN 2563 | |
| 40.1 GPa @Temperature 50.0 °C |
5810 ksi @Temperature 122 °F |
Flexure Weft; 13 min @ 250°F; prEN 2563 | |
| Shear Strength | 68.1 MPa @Temperature 50.0 °C |
9870 psi @Temperature 122 °F |
ILSS Weft; 15 min @ 250°F |
| 68.1 MPa @Temperature 50.0 °C |
9870 psi @Temperature 122 °F |
ILSS Weft; 30 min @ 250°F | |
| 69.02 MPa @Temperature 50.0 °C |
10010 psi @Temperature 122 °F |
ILSS Weft; 10 min @ 250°F | |
| 80.0 MPa @Temperature 22.8 °C |
11600 psi @Temperature 73.0 °F |
ILSS Weft; 10 min @ 250°F | |
| 80.0 MPa @Temperature 22.8 °C |
11600 psi @Temperature 73.0 °F |
ILSS Weft; 15 min @ 250°F | |
| 80.0 MPa @Temperature 22.8 °C |
11600 psi @Temperature 73.0 °F |
ILSS Weft; 30 min @ 250°F |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC K5040 E30 Polypropylene Copolymer, Mineral Reinforced, Elastomer Modified
- Qualchem Danamid FGFS-30 Polyamide 6, 30% Glass Fiber
- ExxonMobil Escorene® LD-133 LDPE Packaging Film Resin (discontinued **)
- LyondellBasell Pro-fax 7823 Polypropylene Impact Copolymer, Fractional Melt Flow
- Latrobe Lescalloy® HP 9-4-30 VAC-ARC ; 5.75 in RCS Billet Size High Strength Alloy Steel
- SSAB Tunnplat Domex® 024 BOR Water quenched Boron Steel
- Star Plastics ABSGF20 Molding Grade ABS With 20% Glass
- Williams Advanced Alloys C109 Solder
- 3M FM017 Indoor UL Recognized Clear Polyester Overlaminate Label Product
- BASF Procom® D 1133 Polypropylene
Copyright © lookpolymers.com All Rights Reserved