Category | Metal , Nonferrous Metal , Nickel Alloy |
Manufacturer | Haynes International, Inc. |
Trade Name | |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Haynes 282® Nickel Alloy Sheet, Gamma-Prime Strengthened.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 8.27 g/cc | 0.299 lb/in³ | Solution Annealed |
8.29 g/cc | 0.299 lb/in³ | Age-hardened |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 975 MPa @Treatment Temp. 871 °C, Time 3.60e+6 sec |
141000 psi @Treatment Temp. 1600 °F, Time 1000 hour |
Room temp test after thermal exposure |
1102 MPa @Treatment Temp. 816 °C, Time 3.60e+6 sec |
159800 psi @Treatment Temp. 1500 °F, Time 1000 hour |
Room temp test after thermal exposure | |
1176 MPa @Treatment Temp. 760 °C, Time 3.60e+6 sec |
170600 psi @Treatment Temp. 1400 °F, Time 1000 hour |
Room temp test after thermal exposure | |
1191 MPa @Treatment Temp. 649 °C, Time 3.60e+6 sec |
172700 psi @Treatment Temp. 1200 °F, Time 1000 hour |
Room temp test after thermal exposure | |
Tensile Strength, Yield | 502 MPa @Treatment Temp. 502 °C, Time 3.60e+6 sec |
72800 psi @Treatment Temp. 936 °F, Time 1000 hour |
0.2%. Room temp test after thermal exposure |
634 MPa @Treatment Temp. 634 °C, Time 3.60e+6 sec |
92000 psi @Treatment Temp. 1170 °F, Time 1000 hour |
0.2%. Room temp test after thermal exposure | |
718 MPa @Treatment Temp. 718 °C, Time 3.60e+6 sec |
104000 psi @Treatment Temp. 1320 °F, Time 1000 hour |
0.2%. Room temp test after thermal exposure | |
778 MPa @Treatment Temp. 778 °C, Time 3.60e+6 sec |
113000 psi @Treatment Temp. 1430 °F, Time 1000 hour |
0.2%. Room temp test after thermal exposure | |
Elongation at Break | 22.3 % @Treatment Temp. 634 °C, Time 3.60e+6 sec |
22.3 % @Treatment Temp. 1170 °F, Time 1000 hour |
Room temp test after thermal exposure |
22.8 % @Treatment Temp. 718 °C, Time 3.60e+6 sec |
22.8 % @Treatment Temp. 1320 °F, Time 1000 hour |
Room temp test after thermal exposure | |
24.2 % @Treatment Temp. 502 °C, Time 3.60e+6 sec |
24.2 % @Treatment Temp. 936 °F, Time 1000 hour |
Room temp test after thermal exposure | |
25.8 % @Treatment Temp. 778 °C, Time 3.60e+6 sec |
25.8 % @Treatment Temp. 1430 °F, Time 1000 hour |
Room temp test after thermal exposure | |
Creep Strength | 34.0 MPa @Temperature 927 °C, Time 3.60e+6 sec |
4930 psi @Temperature 1700 °F, Time 1000 hour |
1% Creep |
62.0 MPa @Temperature 927 °C, Time 360000 sec |
8990 psi @Temperature 1700 °F, Time 100 hour |
1% Creep | |
69.0 MPa @Temperature 871 °C, Time 3.60e+6 sec |
10000 psi @Temperature 1600 °F, Time 1000 hour |
1% Creep | |
124 MPa @Temperature 871 °C, Time 360000 sec |
18000 psi @Temperature 1600 °F, Time 100 hour |
1% Creep | |
145 MPa @Temperature 816 °C, Time 3.60e+6 sec |
21000 psi @Temperature 1500 °F, Time 1000 hour |
1% Creep | |
221 MPa @Temperature 816 °C, Time 360000 sec |
32100 psi @Temperature 1500 °F, Time 100 hour |
1% Creep | |
241 MPa @Temperature 760 °C, Time 3.60e+6 sec |
35000 psi @Temperature 1400 °F, Time 1000 hour |
1% Creep | |
331 MPa @Temperature 760 °C, Time 360000 sec |
48000 psi @Temperature 1400 °F, Time 100 hour |
1% Creep | |
365 MPa @Temperature 704 °C, Time 3.60e+6 sec |
52900 psi @Temperature 1300 °F, Time 1000 hour |
1% Creep | |
496 MPa @Temperature 704 °C, Time 360000 sec |
71900 psi @Temperature 1300 °F, Time 100 hour |
1% Creep | |
545 MPa @Temperature 649 °C, Time 3.60e+6 sec |
79000 psi @Temperature 1200 °F, Time 1000 hour |
1% Creep | |
Rupture Strength | 41.0 MPa @Temperature 927 °C, Time 3.60e+6 sec |
5950 psi @Temperature 1700 °F, Time 1000 hour |
|
83.0 MPa @Temperature 927 °C, Time 360000 sec |
12000 psi @Temperature 1700 °F, Time 100 hour |
||
83.0 MPa @Temperature 871 °C, Time 3.60e+6 sec |
12000 psi @Temperature 1600 °F, Time 1000 hour |
||
152 MPa @Temperature 871 °C, Time 360000 sec |
22000 psi @Temperature 1600 °F, Time 100 hour |
||
159 MPa @Temperature 816 °C, Time 3.60e+6 sec |
23100 psi @Temperature 1500 °F, Time 1000 hour |
||
255 MPa @Temperature 816 °C, Time 360000 sec |
37000 psi @Temperature 1500 °F, Time 100 hour |
||
262 MPa @Temperature 760 °C, Time 3.60e+6 sec |
38000 psi @Temperature 1400 °F, Time 1000 hour |
||
386 MPa @Temperature 760 °C, Time 360000 sec |
56000 psi @Temperature 1400 °F, Time 100 hour |
||
386 MPa @Temperature 704 °C, Time 3.60e+6 sec |
56000 psi @Temperature 1300 °F, Time 1000 hour |
||
517 MPa @Temperature 704 °C, Time 360000 sec |
75000 psi @Temperature 1300 °F, Time 100 hour |
||
552 MPa @Temperature 649 °C, Time 3.60e+6 sec |
80100 psi @Temperature 1200 °F, Time 1000 hour |
||
Modulus of Elasticity | 140 GPa @Temperature 1000 °C |
20300 ksi @Temperature 1830 °F |
Dynamic |
154 GPa @Temperature 900 °C |
22300 ksi @Temperature 1650 °F |
Dynamic | |
166 GPa @Temperature 800 °C |
24100 ksi @Temperature 1470 °F |
Dynamic | |
175 GPa @Temperature 700 °C |
25400 ksi @Temperature 1290 °F |
Dynamic | |
183 GPa @Temperature 600 °C |
26500 ksi @Temperature 1110 °F |
Dynamic | |
190 GPa @Temperature 500 °C |
27600 ksi @Temperature 932 °F |
Dynamic | |
196 GPa @Temperature 400 °C |
28400 ksi @Temperature 752 °F |
Dynamic | |
202 GPa @Temperature 300 °C |
29300 ksi @Temperature 572 °F |
Dynamic | |
209 GPa @Temperature 200 °C |
30300 ksi @Temperature 392 °F |
Dynamic | |
213 GPa @Temperature 100 °C |
30900 ksi @Temperature 212 °F |
Dynamic | |
217 GPa @Temperature 25.0 °C |
31500 ksi @Temperature 77.0 °F |
Dynamic | |
Poissons Ratio | 0.319 @Temperature 25.0 °C |
0.319 @Temperature 77.0 °F |
|
0.326 @Temperature 100 °C |
0.326 @Temperature 212 °F |
||
0.335 @Temperature 200 °C |
0.335 @Temperature 392 °F |
||
0.335 @Temperature 300 °C |
0.335 @Temperature 572 °F |
||
0.337 @Temperature 400 °C |
0.337 @Temperature 752 °F |
||
0.341 @Temperature 500 °C |
0.341 @Temperature 932 °F |
||
0.346 @Temperature 600 °C |
0.346 @Temperature 1110 °F |
||
0.352 @Temperature 700 °C |
0.352 @Temperature 1290 °F |
||
0.355 @Temperature 800 °C |
0.355 @Temperature 1470 °F |
||
0.357 @Temperature 900 °C |
0.357 @Temperature 1650 °F |
||
0.363 @Temperature 1000 °C |
0.363 @Temperature 1830 °F |
||
Shear Modulus | 51.0 GPa @Temperature 1000 °C |
7400 ksi @Temperature 1830 °F |
Dynamic |
57.0 GPa @Temperature 900 °C |
8270 ksi @Temperature 1650 °F |
Dynamic | |
61.0 GPa @Temperature 800 °C |
8850 ksi @Temperature 1470 °F |
Dynamic | |
65.0 GPa @Temperature 700 °C |
9430 ksi @Temperature 1290 °F |
Dynamic | |
68.0 GPa @Temperature 600 °C |
9860 ksi @Temperature 1110 °F |
Dynamic | |
71.0 GPa @Temperature 500 °C |
10300 ksi @Temperature 932 °F |
Dynamic | |
73.0 GPa @Temperature 400 °C |
10600 ksi @Temperature 752 °F |
Dynamic | |
76.0 GPa @Temperature 300 °C |
11000 ksi @Temperature 572 °F |
Dynamic | |
78.0 GPa @Temperature 200 °C |
11300 ksi @Temperature 392 °F |
Dynamic | |
80.0 GPa @Temperature 100 °C |
11600 ksi @Temperature 212 °F |
Dynamic | |
82.0 GPa @Temperature 25.0 °C |
11900 ksi @Temperature 77.0 °F |
Dynamic |