Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750)

Category Metal , Nonferrous Metal , Nickel Alloy
Manufacturer Haynes International, Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes X-750 Nickel Alloy Sheet and Strip (AMS 5598, UNS N07750).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Haynes X-750 (UNS No. N07750) alloy is an age-hardenable, nickel-base superalloy with very good strength at temperatures up to about 1600°F (870°C). It is widely used as a wrought material for forged and fabricated parts in aerospace and industrial applications. Its strength is somewhat less that that for Haynes 718 alloy up to about 1400°F (760°C), and lower than that for Haynes R-41 alloy at higher temperatures. Alloy X-750 can be cold-formed in the annealed condition, and may also be hot-formed at temperatures of about 1900°F (1040°C) or above. Weldability is somewhat limited by susceptibility to strain age cracking under conditions of heavy restraint. The alloy exhibits good resistance to oxidizing combustion gas environments at temperatures up to about 1600°F (870°C).Property data for samples Heat-treated at 1900°F(1040°C) and 1350°F(730°C)/8hr/FC to 1150°F(620°C)/8hr/AC.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.26 g/cc
0.298 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 115 MPa

@Temperature 980 °C
 16700 psi

@Temperature 1800 °F
360 MPa

@Temperature 870 °C
 52200 psi

@Temperature 1600 °F
650 MPa

@Temperature 760 °C
 94300 psi

@Temperature 1400 °F
990 MPa

@Temperature 650 °C
 144000 psi

@Temperature 1200 °F
1120 MPa

@Temperature 540 °C
 162000 psi

@Temperature 1000 °F
1325 MPa

@Temperature 25.0 °C
 192200 psi

@Temperature 77.0 °F
Tensile Strength, Yield 63.0 MPa

@Strain 0.200 %,
Temperature 980 °C
 9140 psi

@Strain 0.200 %,
Temperature 1800 °F
295 MPa

@Strain 0.200 %,
Temperature 870 °C
 42800 psi

@Strain 0.200 %,
Temperature 1600 °F
635 MPa

@Strain 0.200 %,
Temperature 760 °C
 92100 psi

@Strain 0.200 %,
Temperature 1400 °F
835 MPa

@Strain 0.200 %,
Temperature 650 °C
 121000 psi

@Strain 0.200 %,
Temperature 1200 °F
860 MPa

@Strain 0.200 %,
Temperature 540 °C
 125000 psi

@Strain 0.200 %,
Temperature 1000 °F
975 MPa

@Strain 0.200 %,
Temperature 25.0 °C
 141000 psi

@Strain 0.200 %,
Temperature 77.0 °F
Elongation at Break 2.5 %

@Temperature 760 °C
 2.5 %

@Temperature 1400 °F
 2-inch (51 mm) sample
5.8 %

@Temperature 650 °C
 5.8 %

@Temperature 1200 °F
 2-inch (51 mm) sample
8.0 %

@Temperature 870 °C
 8.0 %

@Temperature 1600 °F
 2-inch (51 mm) sample
22.2 %

@Temperature 540 °C
 22.2 %

@Temperature 1000 °F
 2-inch (51 mm) sample
23.6 %

@Temperature 25.0 °C
 23.6 %

@Temperature 77.0 °F
 2-inch (51 mm) sample
42 %

@Temperature 980 °C
 42 %

@Temperature 1800 °F
 2-inch (51 mm) sample
Rupture Strength 45.0 MPa

@Temperature 925 °C,
Time 36000 sec
 6530 psi

@Temperature 1700 °F,
Time 10.0 hour
 Initial Stress
46.0 MPa

@Temperature 870 °C,
Time 360000 sec
 6670 psi

@Temperature 1600 °F,
Time 100 hour
 Initial Stress
51.0 MPa

@Temperature 815 °C,
Time 3.60e+6 sec
 7400 psi

@Temperature 1500 °F,
Time 1000 hour
 Initial Stress
86.0 MPa

@Temperature 870 °C,
Time 36000 sec
 12500 psi

@Temperature 1600 °F,
Time 10.0 hour
 Initial Stress
97.0 MPa

@Temperature 815 °C,
Time 360000 sec
 14100 psi

@Temperature 1500 °F,
Time 100 hour
 Initial Stress
105 MPa

@Temperature 760 °C,
Time 3.60e+6 sec
 15200 psi

@Temperature 1400 °F,
Time 1000 hour
 Initial Stress
165 MPa

@Temperature 815 °C,
Time 36000 sec
 23900 psi

@Temperature 1500 °F,
Time 10.0 hour
 Initial Stress
180 MPa

@Temperature 760 °C,
Time 360000 sec
 26100 psi

@Temperature 1400 °F,
Time 100 hour
 Initial Stress
200 MPa

@Temperature 705 °C,
Time 3.60e+6 sec
 29000 psi

@Temperature 1300 °F,
Time 1000 hour
 Initial Stress
285 MPa

@Temperature 760 °C,
Time 36000 sec
 41300 psi

@Temperature 1400 °F,
Time 10.0 hour
 Initial Stress
310 MPa

@Temperature 705 °C,
Time 360000 sec
 45000 psi

@Temperature 1300 °F,
Time 100 hour
 Initial Stress
345 MPa

@Temperature 650 °C,
Time 3.60e+6 sec
 50000 psi

@Temperature 1200 °F,
Time 1000 hour
 Initial Stress
420 MPa

@Temperature 705 °C,
Time 36000 sec
 60900 psi

@Temperature 1300 °F,
Time 10.0 hour
 Initial Stress
455 MPa

@Temperature 650 °C,
Time 360000 sec
 66000 psi

@Temperature 1200 °F,
Time 100 hour
 Initial Stress
490 MPa

@Temperature 600 °C,
Time 3.60e+6 sec
 71100 psi

@Temperature 1110 °F,
Time 1000 hour
 Initial Stress
550 MPa

@Temperature 650 °C,
Time 36000 sec
 79800 psi

@Temperature 1200 °F,
Time 10.0 hour
 Initial Stress
585 MPa

@Temperature 600 °C,
Time 360000 sec
 84800 psi

@Temperature 1110 °F,
Time 100 hour
 Initial Stress
825 MPa

@Temperature 600 °C,
Time 36000 sec
 120000 psi

@Temperature 1110 °F,
Time 10.0 hour
 Initial Stress
Modulus of Elasticity 138 GPa

@Temperature 1000 °C
 20000 ksi

@Temperature 1830 °F
 Dynamic
152 GPa

@Temperature 900 °C
 22000 ksi

@Temperature 1650 °F
 Dynamic
165 GPa

@Temperature 800 °C
 23900 ksi

@Temperature 1470 °F
 Dynamic
176 GPa

@Temperature 700 °C
 25500 ksi

@Temperature 1290 °F
 Dynamic
184 GPa

@Temperature 600 °C
 26700 ksi

@Temperature 1110 °F
 Dynamic
189 GPa

@Temperature 400 °C
 27400 ksi

@Temperature 752 °F
 Dynamic
201 GPa

@Temperature 200 °C
 29200 ksi

@Temperature 392 °F
 Dynamic
214 GPa

@Temperature 20.0 °C
 31000 ksi

@Temperature 68.0 °F
 Dynamic
Thermal Properties Metric English Comments
CTE, linear 14.3 µm/m-°C

@Temperature 20.0 - 500 °C
 7.94 µin/in-°F

@Temperature 68.0 - 932 °F
14.8 µm/m-°C

@Temperature 20.0 - 600 °C
 8.22 µin/in-°F

@Temperature 68.0 - 1110 °F
15.5 µm/m-°C

@Temperature 20.0 - 700 °C
 8.61 µin/in-°F

@Temperature 68.0 - 1290 °F
16.3 µm/m-°C

@Temperature 20.0 - 800 °C
 9.06 µin/in-°F

@Temperature 68.0 - 1470 °F
17.4 µm/m-°C

@Temperature 20.0 - 900 °C
 9.67 µin/in-°F

@Temperature 68.0 - 1650 °F
17.9 µm/m-°C

@Temperature 20.0 - 1000 °C
 9.94 µin/in-°F

@Temperature 68.0 - 1830 °F
Thermal Conductivity 14.1 W/m-K

@Temperature 200 °C
 97.9 BTU-in/hr-ft²-°F

@Temperature 392 °F
16.9 W/m-K

@Temperature 400 °C
 117 BTU-in/hr-ft²-°F

@Temperature 752 °F
19.8 W/m-K

@Temperature 600 °C
 137 BTU-in/hr-ft²-°F

@Temperature 1110 °F
21.3 W/m-K

@Temperature 700 °C
 148 BTU-in/hr-ft²-°F

@Temperature 1290 °F
22.7 W/m-K

@Temperature 800 °C
 158 BTU-in/hr-ft²-°F

@Temperature 1470 °F
24.0 W/m-K

@Temperature 900 °C
 167 BTU-in/hr-ft²-°F

@Temperature 1650 °F
Melting Point 1395 - 1425 °C
2543 - 2597 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.000121 ohm-cm

@Temperature 20.0 °C
 0.000121 ohm-cm

@Temperature 68.0 °F
0.000124 ohm-cm

@Temperature 200 °C
 0.000124 ohm-cm

@Temperature 392 °F
0.000125 ohm-cm

@Temperature 400 °C
 0.000125 ohm-cm

@Temperature 752 °F
0.000126 ohm-cm

@Temperature 900 °C
 0.000126 ohm-cm

@Temperature 1650 °F
0.000128 ohm-cm

@Temperature 800 °C
 0.000128 ohm-cm

@Temperature 1470 °F
0.000129 ohm-cm

@Temperature 700 °C
 0.000129 ohm-cm

@Temperature 1290 °F
0.000130 ohm-cm

@Temperature 600 °C
 0.000130 ohm-cm

@Temperature 1110 °F