Grupo Repol Dinalon® A1S25 G50 PA66 50% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® A1S25 G50 PA66 50% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
| Flexural Strength | 325 MPa | 47100 psi | ISO 178 |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 |
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/A |
| Vicat Softening Point | >= 230 °C | >= 446 °F | 50N; ISO 306 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC TS15020E Polypropylene Copolymer, Mineral Reinforced
- SABIC Innovative Plastics GELOY XP4025 ASA+PC (Asia Pacific)
- Hyosung Topilene HJ541CP PP
- A. Schulman CP842-01 Hexene Copolymer LLDPE Resin
- American Elements Nickel Titanium Nanoparticles
- Fainplast Compounds HL 91 Flexible PVC, Insulation for High Temperatures
- Arlon 51986R015 0.0165" (0.419 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- BASF Ultramid® A3Z BK 30464 PA66 (Conditioned)
- Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved