Gromax BFG50-FU00B3 Nylon 6 49.4% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG50-FU00B3 Nylon 6 49.4% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.67 g/cc | 1.67 g/cc | ISO 1183 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Melt Flow | 32.3 g/10 min @Load 5.00 kg, Temperature 275 °C |
32.3 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 196.3 MPa | 28480 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.0 % | 3.0 % | 50 mm/min; ISO 527 |
| Flexural Strength | 314.3 MPa | 45590 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 13.1 GPa | 1910 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 146.7 kJ/m² | 69.81 ft-lb/in² | ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216.7 °C | 422.1 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 276 - 290 °C | 529 - 554 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ PP2001 Polypropylene with 2 wt% Multi-Wall Carbon Nanotubes
- Pau Tai Super fine zinc stearate, Monomer Stabilizer
- Fluorseals PTFE 15% graphite filled
- Karina E 85/209-D-AT-IS-SI Clear PVC Compound
- A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- ChevronTexaco ISO 15 Handy Oil
- A. Schulman ComAlloy Hiloy® 623 Nylon 6/6, Glass Reinforced, Flow Enhanced, UL
- 3M Scotch® 8884 Stretchable Tape
- BASF Ultramid® C3U BK23079 PA66/6 (Dry)
- DuPont Elvax® 4355 Ethylene Vinyl Acetate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved