Gromax BFG50-AH00B2 Nylon 6 50% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG50-AH00B2 Nylon 6 50% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ISO 1183 |
| Moisture Absorption | 0.700 % | 0.700 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Temperature 80.0 °C |
0.0020 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Temperature 80.0 °C |
0.0060 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 275 °C |
20 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 98 | 98 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 208 MPa | 30200 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.0 % | 3.0 % | 50 mm/min; ISO 527 |
| Flexural Strength | 350 MPa | 50800 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 12.7 GPa | 1850 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 9.60 J/cm² @Temperature 23.0 °C |
45.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.82 J/cm² @Temperature 23.0 °C |
8.66 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Nylene® Vexel™ B12GF15 , 15% Glass Reinforced PBT
- Osprey Metals H13 Tool Steel Powder (Grade 80% - 22)
- SABIC Innovative Plastics Lexan® PC0700 PC (Asia Pacific)
- Huntsman Araldite GY 6008 Bisphenol A Epoxy Liquid Resin
- Haysite Heatmeiser® H340 Platen Insulation
- A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene
- Universal Wire Works Nichrome V (AMS 5676) Nickel Alloy Filler Metal
- TPI Porene® ABS-GA803 High Gloss, UV Resistant ABS Resin
- ExxonMobil Escorene® LD 755.12 Molding, extrusion and compounding resin
- Parker Chomerics CHO-SEAL 1215 Conductive Elastomer
Copyright © lookpolymers.com All Rights Reserved