Greene Tweed FLUORAZ® 790 Fluoroelastomer, FEPM
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Greene Tweed |
| Trade Name | FLUORAZ® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Greene Tweed FLUORAZ® 790 Fluoroelastomer, FEPM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Greene, Tweed`s Fluoraz® functions effortlessly in a variety of challenging process environments. Fluoraz performs well in aggressive chemicals where ultrapure materials are not required. Known for its capabilities in high-temperature environments and its chemical resistance, Greene, Tweed`s Fluoraz has proven field performance in both dynamic and static applications.Information provided by Greene Tweed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 84 | 84 | After 70hrs @347°F in Stauffer 7700 |
| 95 | 95 | ASTM D2240 | |
| Tensile Strength at Break | 17.62 MPa | 2555 psi | After 70hrs @347°F in Stauffer 7700 |
| 24.1 MPa | 3500 psi | ASTM D1414 | |
| Tensile Strength, Yield | 10.7 MPa | 1550 psi | @50% Elongation; ASTM D1414 |
| Elongation at Break | 125 % | 125 % | ASTM D1414 |
| 160 % | 160 % | After 70hrs @347°F in Stauffer 7700 | |
| Compression Set | 27 % | 27 % | 166 hours @ 347°F @ 25% deflection; ASTM D395 |
| 16 % @Temperature 23.0 °C |
16 % @Temperature 73.4 °F |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -6.67 °C | 20.0 °F | |
| Shrinkage | -21.0 % @Temperature 175 °C, Time 252000 sec |
-21.0 % @Temperature 347 °F, Time 70.0 hour |
in Stauffer 7700 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics XYLEX X7503 PC+POLYESTER (Asia Pacific)
- Total PS CPDS FT875 Flame Retardant Polystyrene
- Plastics Group Polifil® GFPP-30 30% Glass-Reinforced Polypropylene
- Elgiloy® Co-Cr-Ni Alloy, Strip, 65% Cold Reduction, Heat Treated
- ExxonMobil LDPE LD 361HF Low Density Polyethylene Resin
- Multibase Multi-ABS 3246 High Flow Grade
- Shinkong Synthetic Fibers Shinite® PP4210 PP, Fire Retardant
Copyright © lookpolymers.com All Rights Reserved