Fibre Glast RAE 2426 / 2177 Epoxy (discontinued **)
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fibre Glast RAE 2426 / 2177 Epoxy
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Fibre Glast Developments Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Viscosity | 680 cP | 680 cP | ASTM D2293 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 89 | 89 | Cured; ASTM D2240 |
| Tensile Strength at Break | 275.0 MPa | 39880 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Elongation at Break | 1.87 % | 1.87 % | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Tensile Modulus | 16.8 GPa | 2440 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content. |
| Flexural Strength | 374.69 MPa | 54344 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Flexural Modulus | 19.2 GPa | 2780 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 62.8 °C | 145 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Pot Life | 60.0 min @Temperature 25.0 °C |
60.0 min @Temperature 77.0 °F |
4 fl. Oz.; ASTM D2471 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mix Ratio | 100:21 | Resin:Hardener by Weight |
| 4:1 | Resin:Hardener by Volume |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® SH230S33 Silver-Coated Hollow Glass Spheres
- Total Finathene® DF 210 HDPE resin (discontinued **)
- Multibase Multi-Flex® TPE A 3104-10 AGATE 5ES
- SABIC Innovative Plastics LNP Thermocomp RFZ349 PA 66 (Asia Pacific)
- Styron XZ 97219.00 Carboxylated SB
- Teknor Apex Monprene® MP-1679L2 Thermoplastic Elastomer
- BNZ Materials BNZ-24 Insulating Firebrick
- Akro-Plastic Akromid® T6 GF30 (3501) PPA Conditioned, 30% Glass Filled
- Bhansali Engineering Abstron KU-650 ABS Super Heat Resistant
- Schmolz + Bickenbach Cryodur® 2510 (O-1) Cold Work Die Steel
Copyright © lookpolymers.com All Rights Reserved