Fibre Glast ProSet 125R / 229H Epoxy (discontinued **)
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fibre Glast ProSet 125R / 229H Epoxy
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Fibre Glast Developments Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Viscosity | 325 cP | 325 cP | ASTM D2293 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 89 | 89 | Cured; ASTM D2240 |
| Tensile Strength at Break | 295.2 MPa | 42810 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Elongation at Break | 2.04 % | 2.04 % | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 |
| Tensile Modulus | 16.8 GPa | 2430 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content. |
| Flexural Strength | 383.08 MPa | 55561 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Flexural Modulus | 19.6 GPa | 2840 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | 63.3 °C | 146 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Pot Life | 90.0 min @Temperature 25.0 °C |
90.0 min @Temperature 77.0 °F |
4 fl. Oz.; ASTM D2471 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mix Ratio | 100:30 | Resin:Hardener by Weight |
| 2.86:1 | Resin:Hardener by Volume |
Users viewing this material also viewed the following:
- PSM Industries PolyAlloys MIM-WC-6Co Tungsten Carbide
- PolyOne Dynaflex™ G7950-1 NSFG Thermoplastic Elastomer (TPE)
- Gromax BTQ50-DQ00N1 Nylon 6, Impact Modified (Dry)
- Denka VINYKON W4029 PVC, W grade for equipment cords, for heat resistance
- 3M 4496W Double Coated Polyethylene Foam Tape
- BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry)
- Advanced Polymer Alloys DuraGrip™ 6070 BK Thermoplastic Elastomer
- ATI Allvac® Astroloy Nickel Superalloy, Heat Treatment: 1163°C (2125°F) + Age
- A. Schulman ComAlloy Hiloy® 131 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled
- Buckeye Polymers BP RPP 1009 GK Polypropylene, 10% Glass Filled
Copyright © lookpolymers.com All Rights Reserved