- Fiberfil® PP-60/TC/13 BL8860 Polypropylene Homopolymer, 13% Talc Filled
Fiberfil® PP-60/TC/13 BL8860 Polypropylene Homopolymer, 13% Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/TC/13 BL8860 Polypropylene Homopolymer, 13% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.013 cm/cm @Thickness 3.17 mm |
0.013 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.020 cm/cm @Thickness 6.35 mm |
0.020 in/in @Thickness 0.250 in |
ASTM D955 | |
| 0.030 cm/cm @Thickness 12.7 mm |
0.030 in/in @Thickness 0.500 in |
ASTM D955 | |
| Melt Flow | 13 g/10 min | 13 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 - 95 | 90 - 95 | ASTM D785 |
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Elongation at Yield | 25 % | 25 % | ASTM D638 |
| Tensile Modulus | 2.34 GPa | 340 ksi | ASTM D638 |
| Flexural Strength | 48.3 MPa | 7000 psi | ASTM D790 |
| Flexural Modulus | 2.21 GPa | 320 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Front Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | |
| Mold Temperature | 32.2 - 71.1 °C | 90.0 - 160 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GA-96-120 PVC Compound
- Orion Engineered Carbons CORAX® N 220 ASTM Carbon Black
- Huntsman PE 1008 Film Extrusion Polyethylene (discontinued **)
- PolyOne LubriOne™ NJ-30CF/15T-2S Nylon 12 (discontinued **)
- Global TPO-28T Talc Filled TPO Grade
- SABIC Innovative Plastics LNP LUBRICOMP SG004 PA12 (Europe-Africa-Middle East)
- A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene
- ChevronTexaco ISO 32 AIO
- Arkema Group Nakan® RRS 401 L PVC, Rigid Injection Grade
Copyright © lookpolymers.com All Rights Reserved