Fiberfil® M-2450 Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® M-2450 Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 3.17 mm |
0.010 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | ASTM D638 |
| Elongation at Yield | 77 % | 77 % | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 1.45 GPa | 210 ksi | Secant; ASTM D790 |
| Izod Impact, Notched | 0.246 J/cm @Thickness 3.17 mm |
0.460 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Front Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | |
| Mold Temperature | 37.8 - 71.1 °C | 100 - 160 °F | |
| Back Pressure | 0.345 MPa | 50.0 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics EXTEM VH1003 PEI Copolymer
- Sibur SKS-30 ARKPN 2nd Group Styrene-Butadiene Rubber (SBR)
- Weartech International NOREM 02A Iron Hardfacing & Wear Resistant Alloy
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with TP-90B
- A. Schulman POLYBATCH™ Hot Sauce Red 50323/2 Concentrate Based In LLDPE
- Eurotec® Tecomid® NA40 CR20 BK111 PA6.6, 20% carbon fiber reinforced, black
- BASF Ultramid® A3X2G5 25% Glass Filled PA66 (Dry)
- BASF Elastollan® 1180A10 Wire & Cable Grade Polyurethane Elastomer
- Covestro Bayblend® FR 90 Polycarbonate + ABS Blend, Flame-Retardant (discontinued **)
Copyright © lookpolymers.com All Rights Reserved