ExxonMobil Santoprene® 8211-65 Thermoplastic Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer Exxon Chemical
Trade Name Santoprene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Santoprene® 8211-65 Thermoplastic Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A soft, colorable, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in difficult injection molding applications. This grade of Santoprene 8000 TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding. It is polyolefin based and completely recyclable.Key Features: Non-hygroscopic product, requires little to no drying before processing.Neutral, easy coloring formulation.Recommended for applications requiring excellent ozone resistance.Used in sealing applications.Recommended for applications requiring excellent flex fatigue resistance. UL listed: file #QMFZ2.E80017, Plastics - Component; file #QMFZ8.E80017, Plastics Certified For Canada - Component. Although not NSF certified, this product has a Material Supplier Form on file with NSF to facilitate its evaluation for use in applications requiring NSF certification. EU and China RoHS compliant.Applications:Automotive – InteriorConsumer – Electronics, Speaker Surrounds and Consumer Applications Soft Touch GripsUses:Automotive ApplicationsCell PhonesConsumer ApplicationsFlexible GripsSealsProcessing Method: Blow Molding, Extrusion Blow Molding, Injection Blow Molding, Injection Molding and Multi Injection MoldingAvailability: Africa & Middle East, Europe, North America, Asia Pacific, Latin America and South AmericaInformation provided by ExxonMobile
Physical Properties Metric English Comments
Specific Gravity 0.930 g/cc
0.930 g/cc
23°C; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 68
68
Air at 302°F, 168 hr; ASTM D573
70
70
2 mm, 15 sec; ISO 868
Tensile Strength at Break 0.491 MPa
71.2 psi
Air at 302°F, 168 hr; ASTM D573
5.50 MPa
798 psi
Across Flow; ASTM D412
Tensile Stress 2.50 MPa

@Strain 100 %
363 psi

@Strain 100 %
Across Flow; ASTM D412
Elongation at Break 418.2 %
418.2 %
Air at 302°F, 168 hr; ASTM D573
510 %
510 %
Across Flow; ASTM D412
Compression Set 29 %
29 %
73°F, 70 hr; ASTM D395
55 %
55 %
257°F, 70 hr; ASTM D395
Thermal Properties Metric English Comments
Brittleness Temperature -62.8 °C
-81.0 °F
ASTM D746
UL RTI, Electrical 100 °C
212 °F
UL 746
UL RTI, Mechanical with Impact 90.0 °C

@Thickness 1.10 mm
194 °F

@Thickness 0.0433 in
UL 746
95.0 °C

@Thickness 3.00 mm
203 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 HB

@Thickness 1.10 mm
HB

@Thickness 0.0433 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Processing Properties Metric English Comments
Processing Temperature 175 - 230 °C
347 - 446 °F
Rear Barrel Temperature 177 - 191 °C
351 - 376 °F
Middle Barrel Temperature 179 - 193 °C
354 - 379 °F
Front Barrel Temperature 185 - 199 °C
365 - 390 °F
Nozzle Temperature 185 - 210 °C
365 - 410 °F
Melt Temperature 143 - 216 °C
289 - 421 °F
Processing
Mold Temperature 10.0 - 51.7 °C
50.0 - 125 °F
Processing
Moisture Content 0.080 %
0.080 %
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Clamp Pressure 41.4 - 68.9 MPa
6000 - 10000 psi
Vent Depth 0.00254 cm
0.00100 in
Cushion 0.317 - 0.635 cm
0.125 - 0.250 in
Screw Speed 100 - 200 rpm
100 - 200 rpm
Descriptive Properties Value Comments
Color Natural Color
Form Pellets
Injection Rate Fast
Maximum Regrind % 20
Screw Compression Ratio 2:1 - 2.5:1
Screw L/D Ratio 16:1 - 20:1