DuPont™ Bynel® 22E804 Modified Ethylene Acrylate

Category	Polymer , Thermoplastic , Adhesives, Sealants, and Coatings
Manufacturer	DuPont
Trade Name	Bynel®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont™ Bynel® 22E804 Modified Ethylene Acrylate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BYNEL® Series 2200 resins are modified ethylene acrylate resins. They contain a temperature stable ester which makes them functional in high temperature coextrusions. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. BYNEL 22E804 resin conforms with the Code of Federal Regulations, Title 21, Paragraph 177.1340, covering use in contact with all types of food, subject to meeting the migration limits specified in the regulation.

Physical Properties	Metric	English	Comments
Density	0.940 g/cc	0.0340 lb/in³	ASTM D792, ISO 1183
Melt Flow	5.0 g/10 min @Load 2.16 kg, Temperature 190 °C	5.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238, ISO 1133

Thermal Properties	Metric	English	Comments
Melting Point	93.0 °C	199 °F	ASTM D3418, ISO 3146
Vicat Softening Point	51.0 °C	124 °F	ASTM D1525, ISO 306

Processing Properties	Metric	English	Comments
Processing Temperature	<= 310 °C	<= 590 °F
Feed Temperature	160 °C	320 °F	Blown Film Coextrusion
	160 °C	320 °F	Cast Film/Sheet Processing
Zone 2	185 °C	365 °F	Blown Film Coextrusion
	185 °C	365 °F	Cast Film/Sheet Processing
Zone 3	210 °C	410 °F	Blown Film Coextrusion
	210 °C	410 °F	Cast Film/Sheet Processing
Zone 4	210 °C	410 °F	Blown Film Coextrusion
	235 °C	455 °F	Cast Film/Sheet Processing
Zone 5	210 °C	410 °F	Blown Film Coextrusion
	235 °C	455 °F	Cast Film/Sheet Processing
Adapter Temperature	210 °C	410 °F	Blown Film Coextrusion
	235 °C	455 °F	Cast Film/Sheet Processing
Die Temperature	210 °C	410 °F	Blown Film Coextrusion
	235 °C	455 °F	Cast Film/Sheet Processing
Melt Temperature	210 - 235 °C	410 - 455 °F	CoExtrusion with EVOH Processing
	<= 310 °C	<= 590 °F	CoExtrusion with Nylon Processing