ExxonMobil Paxon™ AG45-004 Blow Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Paxon™ AG45-004 Blow Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AG45-004 is a blow molding high density polyethylene which offers exceptional stress crack resistance and impact performance. It contains an antistat which permits this resin to be used in all food packaging applications.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.945 g/cc	0.0341 lb/in³	ASTM D4883
ESCR 100% Igepal®	>= 1000 hour	>= 1000 hour	ASTM D1693 Condition B
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	17.9 MPa	2600 psi	ASTM D638
Tensile Strength, Yield	24.1 MPa	3500 psi	ASTM D638
Elongation at Break	900 %	900 %	ASTM D638
Elongation at Yield	9.0 %	9.0 %	ASTM D638
Tensile Modulus	1.72 GPa	250 ksi	ASTM D638
Flexural Modulus	1.03 GPa	150 ksi	Method1, Procedure A (1"x3"x0.125"), Tangent calculation; ASTM D790
Tensile Impact Strength	231 kJ/m²	110 ft-lb/in²	ASTM D1822

Thermal Properties	Metric	English	Comments
CTE, linear	120 µm/m-°C @Temperature 20.0 °C	66.7 µin/in-°F @Temperature 68.0 °F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	66.0 °C	151 °F	ASTM D648
Vicat Softening Point	121 °C	250 °F	ASTM D1525
Brittleness Temperature	<= -76.1 °C	<= -105 °F	ASTM D746

Processing Properties	Metric	English	Comments
Melt Temperature	191 °C	375 °F

Descriptive Properties	Value	Comments
Features	Antistat and Thermal Stabilizer