SABIC Innovative Plastics Lexan® SLDM310 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® SLDM310 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral filled Antistatic Polycarbonate, HDT110degC type
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Water Absorption at Saturation | 0.44 % | 0.44 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 20.8 g/10 min @Load 2.16 kg, Temperature 260 °C |
20.8 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Melt Index of Compound | 16 g/10 min @Load 2.16 kg, Temperature 260 °C |
16 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | Type I, 10 mm/min; SABIC - Japan Method |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | Type I, 10 mm/min; SABIC - Japan Method |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 66 % | 66 % | 50 mm/min; ISO 527 |
| 190 % | 190 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Tensile Modulus | 2.66 GPa | 386 ksi | 5 mm/min; ASTM D638 |
| 2.67 GPa | 387 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 2 mm/min; ISO 178 |
| 84.0 MPa | 12200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.50 GPa | 363 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.65 GPa | 384 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.08 J/cm | 2.02 ft-lb/in | ASTM D256 |
| 0.730 J/cm @Temperature -30.0 °C |
1.37 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 116 °C | 241 °F | Rate B/50; ISO 306 |
| 117 °C | 243 °F | Rate B/50; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 9.00e+11 ohm | 9.00e+11 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® OQ2320 PC
- Mar-Bal MB2000-5 Thermoset Polyester Composite Molding Compound
- Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 15 µm)
- Solvay Chemicals Glycerol alpha monochlorohydrin
- Silberline Sparkle Silver Ultraâ„¢ 6756
- A. Schulman PAPERMATCH® H-3818 Specialty Masterbatch
- A. Schulman POLYFORT™ PP 3153 Homopolymer Polypropylene
- Lubrizol ESTANE® GP85AB Ester Based Thermoplastic Polyurethane
- Dow Corning SYL-OFF® PMCPEM 7975 Catalyst Emulsion
- Chevron Phillips Marlex® M248 LLDPE Carbon Black Concentrate
Copyright © lookpolymers.com All Rights Reserved