ExxonMobil Oppalyte™ 50MO747 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Oppalyte™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Oppalyte™ 50MO747 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A white opaque biaxially oriented polypropylene film, coated on one side acrylic, one side PVdC. Provides excellent performance on all packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Broad sealing range on acrylic sideExcellent aroma, oxygen, and moisture barriersSuperior opacity High yieldExcellent stiffnessCoatings are mutually compatible and compatible with converter-applied PVdC coatingsExcellent base for converty-applied coatingsSolvent-free coatingsIdeal support for water-based ink printing on acrylic sideFeatures: Acrylic CoatingFlavor & Aroma BarrierGas BarrierIn Lamination Lap SealableLight BarrierMoisture BarrierOxygen BarrierPVdC CoatedSealable PVcD CoatedApplications:BakeryBiscuits/Cookie/CrackersBox Overwrap Confectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Fresh ProduceFrozen FoodHealth and Beauty Care Household and Detergents Ice Cream Uses:Box Overwrap Flexible PackagingHFFS Flexible Packaging Pre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	0.605 g/m²/day @Temperature 23.0 °C	0.0390 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	3.41 g/m²/day @Temperature 38.0 °C	0.220 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	20.0 cc/m²/day @Temperature 23.0 °C	1.29 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	20.2 cc/m²/day @Temperature 23.0 °C	1.30 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	50.8 microns	2.00 mil	ExxonMobil Method
Coating Weight	32.8 g/m²	20.5 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	130 %	130 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	50 %	50 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.50 GPa	363 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	ExxonMobil Method
	0.35	0.35	ExxonMobil Method
Seal Strength	410 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C	410 g/in @Pressure 40.0 psi, Temperature 284 °F	Otto Brugger, 0.2 sec, PVdC; ExxonMobil Method
	410 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C	410 g/in @Pressure 40.0 psi, Temperature 284 °F	Otto Brugger, 0.2 sec, Acrylic; ExxonMobil Method
Film Tensile Strength at Break, MD	115 MPa	16700 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	170 MPa	24700 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	5.0 % @Temperature 135 °C, Time 432 sec	5.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	5.0 % @Temperature 135 °C, Time 432 sec	5.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Gloss	100 %	100 %	ExxonMobil Method
Transmission, Visible	16.5 %	16.5 %	ExxonMobil Method

Descriptive Properties	Value	Comments
Carbon Dioxide Transmission Rate	5.16 cc/100 in²/ 24 hr	75% RH, ASTM D1434
Heat Seal Range	54°F	PVdC, 36.3 psi, 0.2 sec
	90°F	Acrylic, 36.3 psi, 0.2 sec
Nitrogen Transmission Rate	0.645 cc/100 in²/ 24 hr	75% RH, ASTM D1434
Yield	21000 in²/lb