Techmer ES HiFill® PBT GF20 20% Glass Filled
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PBT GF20 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 20% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 121 MPa | 17500 psi | ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 3.17 mm |
1.60 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.2 µm/m-°C | 14.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 3.00e+16 ohm-cm | 3.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.9 kV/mm | 480 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- MRC Polymers MAXTELâ„¢ 600T18 TPO, 18% Talc Filled
- Huntsman AVALON® 95 AE Thermoplastic Polyurethane
- SSAB Tunnplat Domex® 460MC HSLA Steel
- Universal Wire Works Au-Pd-Ni (AMS 4784) Gold Brazing Filler Metal
- Universal Wire Works Rene 41 (AMS 5800) Filler Metal
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 78A
- Fainplast Compounds MGS 75 Medical Flexible PVC, Injection Molding
- DuPont Performance Polymers Kalrez® 1045 Fluoroelastomer
Copyright © lookpolymers.com All Rights Reserved