ExxonMobil LD 146.NH Cast Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LD 146.NH Cast Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LD 146.NH is a homopolymer film resin offering good clarity, toughness, and stiffness. It is used in food packaging and laminating film.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ExxonMobil Method |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 3.75 g/10 min | 3.75 g/10 min | ExxonMobil Method |
| Antiblock Level | 1200 ppm | 1200 ppm | |
| Slip Level | 900 ppm | 900 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 9.38 MPa | 1360 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.58 MPa | 1390 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 200 % | 200 % | ASTM D882 |
| Film Elongation at Break, TD | 560 % | 560 % | ASTM D882 |
| Film Elongation at Yield, MD | 6.4 % | 6.4 % | ASTM D882 |
| Film Elongation at Yield, TD | 5.5 % | 5.5 % | ASTM D882 |
| Elmendorf Tear Strength MD | 260 g | 260 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 140 g | 140 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 6.823 g/micron | 173.3 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 3.67 g/micron | 93.3 g/mil | ASTM D1922 |
| Dart Drop | 2.36 g/micron | 60.0 g/mil | ASTM D1709 |
| Dart Drop Test | 90.0 g | 0.198 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 21.2 MPa | 3080 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.3 MPa | 2650 psi | ASTM D882 |
| 1% Secant Modulus, MD | 176 MPa | 25500 psi | ASTM D882 |
| 1% Secant Modulus, TD | 212 MPa | 30800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 108 °C | 226 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 95.0 °C | 203 °F | ExxonMobil Method |
| Vicat Softening Point | 91.7 °C | 197 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.5 % | 5.5 % | ASTM D1003 |
| Gloss | 73 % | 73 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- Nye Lubricants 369VF Grease
- Raschig Group SURAPLAST UPA 63 UP
- Lehmann & Voss LUVOCOM® 65-8452-1 PP-copolymer, with aramid reinforcement, lubricant modified
- Greene Tweed CHEMRAZ® SD625 Perfluoroelastomer
- SK Chemicals SKYTHANE® 180A R series Polyurethane
- Polyram PlusTek PB826G3 Nylon 6 for Injection Molding, 15% Glass-fiber Reinforced, Impact Modified and UV Stabilized
- Arlon Thermabond® 99A50X008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- BASF Quadrol® Specialty Polyol
- Polimeri Europa SINKRAL D720 ABS, Impact Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved