Arlon 55279R028 Silicone Rubber/Fiberglass Laminate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 55279R028 Silicone Rubber/Fiberglass Laminate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Interleave: 3 mil PE; Layer 2: uncured silicone rubber; Layer 1: cured silicone rubber; Substrate: 162 fiberglass
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | silicone property; Arlon SQA-TMS-024 |
| Thickness | 88.9 microns | 3.50 mil | layer 1; Arlon SQA-TMS-003 |
| 178 microns | 7.00 mil | layer 2; Arlon SQA-TMS-003 | |
| 483 microns | 19.0 mil | substrate; Arlon SQA-TMS-003 | |
| 749 microns | 29.5 mil | overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
| Elongation at Break | 225 % | 225 % | silicone property; ASTM D412 |
| Adhesive Bond Strength | 0.0545 MPa | 7.90 psi | ASTM D624 |
| Tear Strength | 15.8 kN/m | 90.0 pli | Die B; silicone property; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| UL RTI, Electrical | 200 °C | 392 °F | |
| UL RTI, Mechanical without Impact | 200 °C | 392 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
|
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
||
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hybrid B6720U Polycarbonate + PBT Alloy
- SABIC Innovative Plastics Lexan® 955 PC
- Ineos ABS Lustran® LK197 ABS, Extrusion Grade
- Williams Advanced Alloys WS302 Solder
- EMS-Grivory Grivory® GVX-65 H nat PA*-GF65
- Dynasol Calprene® 375 Solution Random SBR
- Arkema Group OREVAC® 9314 EVA Terpolymer
- A. Schulman ComAlloy Voloy® 411 Mineral Reinforced, PBT Alloy, Flame Retardant, UL
- BASF Paliogen® Blue L 6470 Color Additive
- Zircar Zirconia ZYBF-3 Zirconia Bulk Fiber Insulation
Copyright © lookpolymers.com All Rights Reserved