ExxonMobil Exceed™ 2018EB Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Blow Molding Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 2018EB Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Exceed 2018EB resin is an ethylene based polymer produced with metallocene single site catalysts using ExxonMobil Chemicals Exxpol® Technology. The higher melt index makes this polymer ideally suited for blending into LDPE rich films.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D4703 / D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
Antiblock Level 2500 ppm
2500 ppm
Slip Level 750 ppm
750 ppm
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 480 %
480 %
ASTM D882
Film Elongation at Break, TD 520 %
520 %
ASTM D882
Coefficient of Friction 0.22
0.22
ASTM D1894
Elmendorf Tear Strength, MD 11.0 g/micron
279 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 20.0 g/micron
508 g/mil
ASTM D1922
Dart Drop 30.0 g/micron
762 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ASTM D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ASTM D882
1% Secant Modulus, MD 176 MPa
25500 psi
ASTM D882
1% Secant Modulus, TD 176 MPa
25500 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 118 °C
244 °F
Peak Melting Temperature; ASTM D3418
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ASTM D1003
Gloss 11 %
11 %
60° angle; ASTM D2457
Descriptive Properties Value Comments
Features PPA and Thermal Stabilizer