- SABIC Innovative Plastics LNP LUBRICOMP LCL33 PEEK (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP LUBRICOMP LCL33 PEEK (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP LCL33 PEEK (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* LCL33 is a compound based on Polyethereketone resin containg Carbon Fiber, PTFE. Added features include: Elecrtically Conductive , Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 162 MPa | 23500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.9 % | 2.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 13.5 GPa | 1960 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 255 MPa | 37000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 12.6 GPa | 1830 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.28 | 0.28 | ASTM D3702 Modified |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 9.50 µm/m-°C @Temperature 23.0 - 60.0 °C |
5.28 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
29.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 300 °C | >= 572 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 ohm - 1e+05 | 1000 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N2000THL Nylon 6 (DAM)
- LG Chemical MB838A Opaque impact modifier
- SABIC Innovative Plastics ULTEM 2100 PEI
- Diamond Polymers PC 1035L Impact Modified, Polycarbonate, Injection Molding Grade
- Fainplast Compounds CL 73/1 Flexible PVC, Sheathing
- Eurostar Staramide PFB33 PA6, 20% Glass Fiber, 10% Glass Bead Filled, Injection Molding Resin
- Dow Nordel® IP 4770P General Purpose Compound
- Addiplast Addilene J 490 S Flame Retardant Polypropylene
- C.O.I.M. EXTER S® S 401 Isophthalic Resin
- Arlon R35948R015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved