Eurotec® Tecopet® PT74 CR30 BK111 PR PET, 30% carbon fiber reinforced, black, fast crystallization grade
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , PET + Carbon Fiber |
| Manufacturer | Eurotec |
| Trade Name | Tecopet® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecopet® PT74 CR30 BK111 PR PET, 30% carbon fiber reinforced, black, fast crystallization grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % @Temperature 23.0 °C |
0.200 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527 |
| Tensile Modulus | 24.0 GPa | 3480 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 250 °C | 482 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 1000 ohm-cm | <= 1000 ohm-cm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |
| Feed Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Throat |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | <= 0.080 % | <= 0.080 % | ISO 960 |
| Hold Pressure | 60.0 - 100 MPa | 8700 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Fast |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND SV713 Conductive Epoxy
- SABIC Innovative Plastics Lexan® ML6018R PC (Asia Pacific)
- Eastman Eastar 5445 PCTG Copolyester, Injection Molded (discontinued **)
- Techmer ES HiFill® HDPE TM30 30% Talc Filled
- SSAB Tunnplat Domex® 280XP Extra High-strength Cold-forming Steel
- Taiwan Sheen Soon Sheenthane® AS-330 TPU for PU Adhesive
- Plenco 1501 Polyester, Briquette, Transfer Molded
- Polyplastics Duracon® M450-44/M450S Acetal Co-polymer (POM), Standard, Super high flow, High cycle
- Arkema Group Rilsan® BECN W3 TL Nylon 11, Sheathing Grade (Conditioned)
- Bulk Molding Compounds BMC 304 Automotive Grade Molding Compound
Copyright © lookpolymers.com All Rights Reserved