Eurotec® Tecomid® NA40 KC50 BK111 PA6.6, 50% glass/carbon fiber reinforced, black
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Black + Glass Fiber Filled |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NA40 KC50 BK111 PA6.6, 50% glass/carbon fiber reinforced, black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Moisture Absorption | 1.30 % @Temperature 23.0 °C |
1.30 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1e+05 | 1e+05 | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Fast |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 3010 X Black Polypropylene
- SABIC Innovative Plastics LNP LUBRICOMP DFL36E PC (Europe-Africa-Middle East)
- DuPont Performance Polymers Crastin® SK615SF NC010 PBT (Unverified Data**)
- SABIC Innovative Plastics Cycoloy® C1000HF PC+ABS (Europe-Africa-Middle East)
- DuPont™ Sclairfilm® GL-3 LLDPE Film, Laminating, 76 µm Thickness (discontinued **)
- SABIC Innovative Plastics NORYL PPX PPX7112 PPE+PP
- A. Schulman PP 1227E-01 Polypropylene High-Impact Polypropylene
- Zeon Chemicals Nipol® 1000x132 Nitrile Elastomer
- Fainplast Compounds PH 58/AL Flexible PVC, Transparent Extrusion
Copyright © lookpolymers.com All Rights Reserved