Eurostar Starglas GX05052 PSU, Glass Fiber Filled
| Category | Polymer , Thermoplastic , Polysulfone (PSU) , Polyphenylsulfone, Glass or Carbon Fiber Reinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starglas |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starglas GX05052 PSU, Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starglas GX05052 is a Glass Fiber Reinforced PSU resin (also known as Starglas PSU A 10V ¾)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 4.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| Tensile Modulus | 4.00 GPa | 580 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 310 - 330 °C | 590 - 626 °F | |
| Zone 2 | 310 - 330 °C | 590 - 626 °F | |
| Zone 3 | 310 - 330 °C | 590 - 626 °F | |
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | |
| Mold Temperature | 150 °C | 302 °F | |
| Drying Temperature | 120 - 150 °C @Time 14400 sec |
248 - 302 °F @Time 4.00 hour |
|
| Moisture Content | 0.050 % | 0.050 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible R4510H Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 (Asia Pacific)
- Teknor Apex Flexalloy® 9100-65 Polyvinyl Chloride Elastomer
- Styron DL 2256LA Carboxylated SB
- DuPont Bynel® 4104 Anhydride-Modified LLDPE Adhesive Resin
- A. Schulman PP 2407 Polypropylene Impact Resistant Copolymer Polypropylene
- Williams Advanced Alloys WS186 Solder
- Dow TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin
- Astro Met ZTA 96 Zirconia Toughened Alumina
Copyright © lookpolymers.com All Rights Reserved