- Eurostar Starflam PX05004 PA66, Glass Fiber Filled, Flame Retardant, Injection Molded
Eurostar Starflam PX05004 PA66, Glass Fiber Filled, Flame Retardant, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam PX05004 PA66, Glass Fiber Filled, Flame Retardant, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PX05004 is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.70 GPa | 827 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 147 MPa | 21300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.30 GPa | 769 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 500 V | >= 500 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 255 - 265 °C | 491 - 509 °F | |
| Zone 2 | 260 - 270 °C | 500 - 518 °F | |
| Zone 3 | 260 - 270 °C | 500 - 518 °F | |
| Melt Temperature | 265 - 275 °C | 509 - 527 °F | |
| Mold Temperature | 55.0 - 95.0 °C | 131 - 203 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Lubrizol Advanced Materials Pearlthane® Clear 15N60D Thermoplastic Polyurethane (discontinued **)
- Huntsman IROGRAN® PS455-200 TPU-Polyester
- SABIC Innovative Plastics Valox® VX5011 PBT (Europe-Africa-Middle East)
- Teknor Apex Sinvicomp SIC 3704 Polyvinyl Chloride, Rigid
- Lubrizol ESTANE® T5417 Ester Based Thermoplastic Polyurethane (European Grade)
- E-Polymers TEKAMID® H12T Unreinforced High Impact PA/ABS Alloy
- Azoty Tarnow™ Tarnamid® T-27 TF10 Polyamide 6 - Improved Slip Properties
- DuPont Performance Polymers VTR 8655 (GBL-S) Peroxide Cured Fluoroelastomer (FKM) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved