Eurostar Staramide PX05046 PA6, Glass Bead/Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled , Nylon 6, Glass Bead Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide PX05046 PA6, Glass Bead/Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide XP05046 is Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | >= 3.0 % | >= 3.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.80 GPa | 841 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.70 GPa | 682 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 250 - 260 °C | 482 - 500 °F | |
| Zone 2 | 265 - 275 °C | 509 - 527 °F | |
| Zone 3 | 265 - 280 °C | 509 - 536 °F | |
| Melt Temperature | 265 - 275 °C | 509 - 527 °F | |
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® E GF 30 PBT, 30% glass fibre
- Polykemi AB POLYblend 83FR PC/ABS-Blend, Flame Retardant, Halogen Free
- Michelman® Michem® Flex HS-333 Water based heat seal coating
- DuPont Performance Polymers Zytel® HTN 51G15HSL NC010 Polyphthalamide (PPA) (Unverified Data**)
- Clariant ABSSP0004 ABS, Chemical Resistant
- BASF Lupragen® N 700 1,8-Diazabicyclo-5,4,0-undecene-7
- 3M 5125 (Clear) Polyethylene Protective Tapes
- Solvay Specialty Polymers Ixef® 5002 Polyarylamide (PARA), 20% GlassPTFE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved