SABIC Innovative Plastics Valox® VX4029 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® VX4029 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX VX4029 is a 30% glass reinforced PBT injection moulding resin with excellent strength, stiffness, dimensional stability and high heat resistance. This grade is a 420 with reduced additive loading.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.26 % @Temperature 23.0 °C |
0.26 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | on tensile bar; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.010 cm/cm | 0.0050 - 0.010 in/in | on tensile bar; SABIC Method |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 g/10 min @Load 4.76 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 13 g/10 min @Load 2.16 kg, Temperature 250 °C |
13 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ISO 2039-2 |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.50 GPa | 1380 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 195 MPa | 28300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| 60.0 kJ/m² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179/2C |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| Taber Abrasion, mg/1000 Cycles | 65 @Load 1.00 kg |
65 @Load 2.20 lb |
CS-17; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 105 µm/m-°C @Temperature 23.0 - 60.0 °C |
58.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 213 °C | 415 °F | Rate B/50; ISO 306 |
| 213 °C | 415 °F | Rate B/120; ISO 306 | |
| 222 °C | 432 °F | Rate A/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
UL 94 by SABIC-IP |
| Oxygen Index | 20 % | 20 % | LOI; ISO 4589 |
| Glow Wire Test | 750 °C @Thickness 1.60 mm |
1380 °F @Thickness 0.0630 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.1 @Frequency 50.0 - 60.0 Hz |
3.1 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz |
0.0010 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 300 V | 300 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Industrial Laminates/Norplex SP525M (WaveMax 5000) Glass Fabric
- Kraton® D1117 P (SIS) Linear Block Copolymer
- LATI Larpeek 50 G/30 PEEK, 30% Glass Fiber Reinforced
- Solvay Specialty Polymers Ixef® HC-1022 Polyarylamide (PARA), 50% Glass Fiber (Dry)
- Shinkong Synthetic Fibers Shinite® D202G15 PBT, 15% Glass Filled, Fire Retardant
- DuPont™ Kevlar® Aramid Pulp
- Chosun Refractories GUN-135L Light-Weight Gunning Castable
- Azoty Tarnow™ Tarnamid® T-27 MCS V0 Polyamide 6 - Flame Retarded, Unreinforced
- Braskem UTEC® 6540 Ultra High Molecular Weight Polyethylene
- 3M 8427-16 Cold Shrink Connector Insulators
Copyright © lookpolymers.com All Rights Reserved