- Sichuan Deyang Haton® hMR61 Polyphenylene Sulfide, Glass & Mineral Reinforced
Sichuan Deyang Haton® hMR61 Polyphenylene Sulfide, Glass & Mineral Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hMR61 Polyphenylene Sulfide, Glass & Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.96 g/cc | 0.0708 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm | 0.0015 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0052 cm/cm | 0.0052 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 107 | 107 | GB/T 3398.2-2008 |
| Tensile Strength | 156 MPa | 22600 psi | GB/T 1040.2-2006 |
| Elongation at Break | 1.0 % | 1.0 % | GB/T1040.2-2006 |
| Flexural Strength | 228 MPa | 33100 psi | GB/T 9341-2008 |
| Flexural Modulus | 18.1 GPa | 2630 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | GB/T 1843-2008 |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.60e+16 ohm-cm | 1.60e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 3.00e+15 ohm | 3.00e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 5.0 | 5.0 | GB/T 1409-2006 |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0010 | 0.0010 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- Mitsui Arlenâ„¢ A315 15% Glass Fiber-Reinforced Modified Nylon 6T (DAM)
- Saint-Gobain CHR® 2995-11R Glass-Foil Backing Silicone Adhesive Pressure Sensitive Tape
- Teknor Apex Beetle® 66GS6 Nylon 66, 30% Glass Bead Reinforced
- Styron DGF080.00 ESU Polypropylene
- Polyram PlusTek PA112NT Nylon 6.6, PTFE Filled
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N550 (FEF) Filler
- BCC Products BC 4578 Polyester Model Board Filler
- 3M 4193-EZ Polyethylene Protective Tapes
- A.D. Compound Adene NTFA Homopolymer 20% Talc Filled Polypropylene
- Ascend Performance Materials Vydyne® R633H Nylon 66/6, 33% Glass Reinforced, Conditioned
Copyright © lookpolymers.com All Rights Reserved