Eastman Tenite 132E-28 Cellulose Acetate (discontinued **)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tenite 132E-28 Cellulose Acetate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
28% Plasticized with 25% fiber grade ester.ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min |
| Elongation at Break | 20 % | 20 % | |
| Elongation at Yield | 3.3 % | 3.3 % | |
| Tensile Modulus | 1.81 GPa | 263 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.02 J/cm² | 4.85 ft-lb/in² | |
| 0.580 J/cm² @Temperature -30.0 °C |
2.76 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.0 µm/m-°C @Temperature 20.0 °C |
46.7 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 133 µm/m-°C @Temperature 20.0 °C |
73.9 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | |
| Vicat Softening Point | 83.0 °C | 181 °F | |
| Glass Transition Temp, Tg | 108 °C | 226 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 240 °C | 428 - 464 °F |
Users viewing this material also viewed the following:
- Niagara LaSalle e.t.d.® 150® Cold Finished Steel Bar
- Heatbath/Park AL-2 Quenching and Tempering Salt
- SABIC Innovative Plastics LNP STAT-KON DE0029 PC (Asia Pacific)
- Teknor Apex Telcar® TL-2635B Thermoplastic Elastomer
- DuPont™ Nomex® E56 Paper, 12 mil Nominal Thickness
- Fainplast Compounds PHA 78 Flexible PVC, Transparent Extrusion
- Arlon R34931R010 0.011" (0.279 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Aremco Ceramabind™ 642-A High Temperature Inorganic Binder
Copyright © lookpolymers.com All Rights Reserved