Eastman Tenite 105-28 Cellulose Acetate (discontinued **)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tenite 105-28 Cellulose Acetate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
28% Plasticized ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50 mm/min |
| Elongation at Break | 19 % | 19 % | |
| Elongation at Yield | 3.5 % | 3.5 % | |
| Tensile Modulus | 2.01 GPa | 292 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.59 J/cm² | 7.57 ft-lb/in² | |
| 0.470 J/cm² @Temperature -30.0 °C |
2.24 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.0 µm/m-°C @Temperature 20.0 °C |
46.7 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 145 µm/m-°C @Temperature 20.0 °C |
80.6 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | |
| Vicat Softening Point | 85.0 °C | 185 °F | |
| Glass Transition Temp, Tg | 95.0 °C | 203 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 240 °C | 428 - 464 °F |
Users viewing this material also viewed the following:
- LG Chemical XR409H ABS, Heat Resistance
- SMAC CABLE® 2514S-20-10 Damping Material
- Teknor Apex Uniprene® UN-7200-73 Thermoplastic Vulcanizate
- Chase Plastics CP Pryme® NN133GL (DAM) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated
- TIMET TIMETAL® 6-2-4-6 Titanium Alloy (Ti-6Al-2Sn-4Zr-6Mo), 10% Equiaxed Alpha + STA
- Goodfellow Iron 91/Silicon 9 Alloy
- Total Lumicene® mPE M 2710 EP Metallocene Polyethylene, Film
- ExxonMobil Santoprene® 271-55 Thermoplastic Elastomer
- Domo 2500H Polypropylene Copolymer
- BASF Elastollan C 88 A TPUR
Copyright © lookpolymers.com All Rights Reserved