EPICHEM Epilon PC UVR Polycarbonate, High Impact
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified , Polycarbonate, UV Stabilized |
| Manufacturer | EPICHEM srl |
| Trade Name | Epilon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM Epilon PC UVR Polycarbonate, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: high fluidity, high impact, UV resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.15 % @Temperature 23.0 °C |
0.15 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Index of Compound | 8.0 - 14 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.0 - 14 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238, ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638, ISO R527 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638, ISO R527 |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 1.00 - 1.80 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
1.87 - 3.37 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM D256, ISO 180/4a |
| 6.00 - 8.00 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
11.2 - 15.0 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 115 °C | 239 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 120 °C | 248 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 140 °C | 284 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Hot Ball Pressure Test | >= 125 °C | >= 257 °F | BS 3456, IEC 335 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 140 - 145 °C @Load 5.00 kg |
284 - 293 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 150 - 155 °C @Load 0.999 kg |
302 - 311 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB - V-2 @Thickness 1.60 mm |
HB - V-2 @Thickness 0.0630 in |
|
| HB - V-2 @Thickness 3.20 mm |
HB - V-2 @Thickness 0.126 in |
||
| Glow Wire Test | 750 °C @Thickness 3.20 mm |
1380 °F @Thickness 0.126 in |
VDE 0471/P2-4, IEC 695 |
| 750 °C @Thickness 2.00 mm |
1380 °F @Thickness 0.0787 in |
VDE 0471/P2-4, IEC 695 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 88 - 90 % | 88 - 90 % | ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.0 @Frequency 1000 Hz |
3.0 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 225 V | 225 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8981 (899-1) (UF) Synthetic Oil
- Techmer ES Electrafil® PS-31/EC BK Polystyrene, Electrically Conductive Carbon Black
- Teknor Apex Monprene® MP-1848R Thermoplastic Elastomer
- ChevronTexaco HDAX® SAE 15W-40
- Dow Prevail® 3150 ABS + Polyurethane
- Eurotec® Tecodur® PB70 GR50 NL100 PBT, 50% glass fiber reinforced, natural
- Aclo Accutech Polypropylene Copolymer CP0437M30L Mica Reinforced
- Arkema Group KYNAR® EXAD 3000 Polyvinylidene Fluoride - Extrusion
- Kraton® G1702 H (SEP) Linear Diblock Copolymer
Copyright © lookpolymers.com All Rights Reserved