EMS-Grivory Grivory® TSGL-60/4 nat PA666-GF60

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 60% Glass Fiber Reinforced
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® TSGL-60/4 nat PA666-GF60.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grilon TSGL-60/4 natural is based on a heat stabilized semi-crystalline Polyamide PA66+PA6 and 60% long glass fibers. Grilon TSGL-60/4 natural is characterized by the following key-properties: high stiffness and strength even after conditioning and over a wide temperature rangeexcellent notched impact resistance also at low temperatureslow creephigh heat distortion temperaturesgood dimensional stability and little warpagegood surface appearance and ease of processing The product has been designed for injection molding of technical parts especially in the area of die-cast metal replacement. Grilon TSGL-60/4 natural is used in the following market segments: automotivemechanical engineeringhousehold and appliances The glass-fibers are aligned in parallel and are just as long as the pellets (usually 10 mm).Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.68 g/cc	0.0607 lb/in³	ISO 1183
Water Absorption	4.0 %	4.0 %	ISO 62
Moisture Absorption	1.20 %	1.20 %	ISO 62
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0020 cm/cm	0.0020 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	230 MPa	33400 psi	conditioned; ISO 2039-1
	340 MPa	49300 psi	dry; ISO 2039-1
Tensile Strength at Break	205 MPa	29700 psi	conditioned; ISO 527-1/-2
	280 MPa	40600 psi	dry; ISO 527-1/-2
Elongation at Break	2.1 %	2.1 %	dry; ISO 527-1/-2
	2.3 %	2.3 %	conditioned; ISO 527-1/-2
Tensile Modulus	16.5 GPa	2390 ksi	conditioned; ISO 527-1/-2
	22.0 GPa	3190 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	11.0 J/cm²	52.3 ft-lb/in²	dry; ISO 179/1eU
	11.5 J/cm²	54.7 ft-lb/in²	conditioned; ISO 179/1eU
	9.50 J/cm² @Temperature 30.0 °C	45.2 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
	10.5 J/cm² @Temperature 30.0 °C	50.0 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
Charpy Impact, Notched	4.00 J/cm²	19.0 ft-lb/in²	dry; ISO 179/1eA
	4.50 J/cm²	21.4 ft-lb/in²	conditioned; ISO 179/1eA
	4.00 J/cm² @Temperature 30.0 °C	19.0 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	4.50 J/cm² @Temperature 30.0 °C	21.4 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C	11.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	40.0 µm/m-°C	22.2 µin/in-°F	ISO 11359-1/-2
Melting Point	260 °C	500 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	120 - 130 °C	248 - 266 °F	long term; EMS
	220 °C	428 °F	short term; EMS
Deflection Temperature at 1.8 MPa (264 psi)	255 °C	491 °F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	235 °C	455 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	conditioned; IEC 60093
	1.00e+13 ohm-cm	1.00e+13 ohm-cm	dry; IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Dielectric Strength	22.0 kV/mm	559 kV/in	conditioned; IEC 60243-1
	27.0 kV/mm	686 kV/in	dry; IEC 60243-1
Comparative Tracking Index	600 V	600 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Automotive electr. and electronics, lighting
	Cooling and climate control
	Exterior
	Interior
	Powertrain and Chassis
Electricals & Electronics	Connectors
	Electrical appliances
	Electrical equipment
	Energy distribution
Form	Granules
Industry & Consumer goods	Housewares
	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
	Sports & Leisure
	Tools & Accessories
Processing	Injection Molding
Product Attributes	Long Fiber Reinforced
Special Characteristics	Improved heat resistance