EMS-Grivory Grivory® TSGL-50/4 black 9833 PA666-GF50

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 40% Glass Fiber Reinforced
Manufacturer	EMS-Grivory (EMS-CHEMIE)
Trade Name	Grivory®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	EMS-Grivory Grivory® TSGL-50/4 black 9833 PA666-GF50.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product description: Grilon TSGL-50/4 black is based on a heat stabilized semicrystalline Polyamide PA66+PA6 and 50% long glass fibers. Grilon TSGL-50/4 black is characterized by the following key-properties: high stiffness and strength even after conditioning and over a wide temperature rangeexcellent notched impact resistance also at low temperatureslow creephigh heat distortion temperaturesgood dimensional stability and little warpagegood surface appearance and ease of processing The product has been designed for injection molding of technical parts especially in the area of die-cast metal replacement. Grilon TSGL-50/4 black is used in the following market segments: automotivemechanical engineeringhousehold and appliances The glass-fibers are aligned in parallel and are just as long as the pellets (usually 10 mm).Information provided by EMS Grivory

Physical Properties	Metric	English	Comments
Density	1.55 g/cc	0.0560 lb/in³	ISO 1183
Water Absorption	4.5 %	4.5 %	ISO 62
Moisture Absorption	1.50 %	1.50 %	ISO 62
Linear Mold Shrinkage, Flow	0.0010 cm/cm	0.0010 in/in	ISO 294-4, 2577
Linear Mold Shrinkage, Transverse	0.0030 cm/cm	0.0030 in/in	ISO 294-4, 2577

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	205 MPa	29700 psi	conditioned; ISO 2039-1
	315 MPa	45700 psi	dry; ISO 2039-1
Tensile Strength at Break	180 MPa	26100 psi	conditioned; ISO 527-1/-2
	255 MPa	37000 psi	dry; ISO 527-1/-2
Elongation at Break	2.0 %	2.0 %	dry; ISO 527-1/-2
	2.3 %	2.3 %	conditioned; ISO 527-1/-2
Tensile Modulus	12.8 GPa	1860 ksi	conditioned; ISO 527-1/-2
	17.8 GPa	2580 ksi	dry; ISO 527-1/-2
Charpy Impact Unnotched	9.50 J/cm²	45.2 ft-lb/in²	dry; ISO 179/1eU
	10.0 J/cm²	47.6 ft-lb/in²	conditioned; ISO 179/1eU
	8.00 J/cm² @Temperature 30.0 °C	38.1 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU
	8.50 J/cm² @Temperature 30.0 °C	40.4 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
Charpy Impact, Notched	3.50 J/cm²	16.7 ft-lb/in²	dry; ISO 179/1eA
	4.00 J/cm²	19.0 ft-lb/in²	conditioned; ISO 179/1eA
	3.50 J/cm² @Temperature 30.0 °C	16.7 ft-lb/in² @Temperature 86.0 °F	dry; ISO 179/1eU
	4.00 J/cm² @Temperature 30.0 °C	19.0 ft-lb/in² @Temperature 86.0 °F	conditioned; ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	20.0 µm/m-°C	11.1 µin/in-°F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	50.0 µm/m-°C	27.8 µin/in-°F	ISO 11359-1/-2
Melting Point	260 °C	500 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	120 - 130 °C	248 - 266 °F	long term; EMS
	220 °C	428 °F	short term; EMS
Deflection Temperature at 1.8 MPa (264 psi)	255 °C	491 °F	ISO 75-1/-2
Deflection Temperature at 8.0 MPa	235 °C	455 °F	ISO 75-1/-2
Flammability, UL94	HB	HB	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+12 ohm-cm	1.00e+12 ohm-cm	conditioned; IEC 60093
	1.00e+13 ohm-cm	1.00e+13 ohm-cm	dry; IEC 60093
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm	IEC 60093
Dielectric Strength	22.0 kV/mm	559 kV/in	conditioned; IEC 60243-1
	27.0 kV/mm	686 kV/in	dry; IEC 60243-1
Comparative Tracking Index	500 V	500 V	conditioned; IEC 60112

Descriptive Properties	Value	Comments
Automotive	Automotive electr. and electronics, lighting
	Cooling and climate control
	Exterior
	Interior
	Powertrain and Chassis
Electricals & Electronics	Connectors
	Electrical appliances
	Electrical equipment
	Energy distribution
Form	Granules
Industry & Consumer goods	Housewares
	Hydraulics & Pneumatics
	Mechanical Engineering
	Power transmission
	Sports & Leisure
	Tools & Accessories
Processing	Injection Molding
Product Attributes	Long Fiber Reinforced
Special Characteristics	Improved heat resistance