EMS-Grivory Grivory® BZ 3 PA6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® BZ 3 PA6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Water Absorption | 9.0 % | 9.0 % | ISO 62 |
| Moisture Absorption | 3.00 % | 3.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 40.0 MPa | 5800 psi | conditioned; ISO 2039-1 |
| 95.0 MPa | 13800 psi | dry; ISO 2039-1 | |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | dry; ISO 527-1/-2 |
| 45.0 MPa | 6530 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 |
| <= 50 % | <= 50 % | dry; ISO 527-1/-2 | |
| Elongation at Yield | 5.0 % | 5.0 % | dry; ISO 527-1/-2 |
| 15 % | 15 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 0.600 GPa | 87.0 ksi | conditioned; ISO 527-1/-2 |
| 1.80 GPa | 261 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU |
| NB | NB | conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 6.00 J/cm² | 28.6 ft-lb/in² | dry; ISO 179/1eA |
| 1.50 J/cm² @Temperature 30.0 °C |
7.14 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 1.50 J/cm² @Temperature 30.0 °C |
7.14 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C | 72.2 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 150 µm/m-°C | 83.3 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 80.0 - 100 °C | 176 - 212 °F | long term; EMS |
| 140 °C | 284 °F | short term; EMS | |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | conditioned; IEC 60243-1 |
| 31.0 kV/mm | 787 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |
| 600 V | 600 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Interior | |
| Powertrain and Chassis | ||
| Electricals & Electronics | Connectors | |
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Mechanical Engineering | ||
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding | |
| Special Characteristics | High impact or impact modified |
Users viewing this material also viewed the following:
- Plasma Coatings 10000 Surface Material
- LG Chemical LUPOY GP2300 PC+GF30%, Heat Resistance
- Chase Plastics CP Pryme® N320GL (COND, 50% RH) Nylon 6 (Utility Grade), 20% Glass Fiber Reinforced, Internally Lubricated
- Tipco Tipcolite® TX 211 Phenolic Compound, Wood Flour, having Medium Flow & High Electrical Properties
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- A. Schulman POLYBATCH™ House Red 50311U/4 Concentrate Based In LLDPE
- ExxonMobil SAE 40 Mobilgard M40 Series
- Alliance Polymers Zythane™ 6080A Thermoplastic Polyurethane Elastomer
- A. Schulman POLYBLAK™ 4692 Premium Black Color Concentrate, 35% Carbon Black Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved