E-Polymers TEKAMID® TA250G45 , 45% Glass Fiber Reinforced PA66, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer E-Polymers Co. Ltd.
Trade Name TEKAMID®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers TEKAMID® TA250G45 , 45% Glass Fiber Reinforced PA66, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
45% Glass Fiber Reinforced, Good surfaceInformation provided by E-Polymers Co. Ltd.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ASTM D792
Water Absorption 0.50 %
0.50 %
23°C/24 hr; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 123
123
ASTM D786
Tensile Strength, Yield 230 MPa
33400 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Flexural Yield Strength 310 MPa
45000 psi
ASTM D790
Flexural Modulus 13.0 GPa
1890 ksi
ASTM D790
Izod Impact, Notched 1.50 J/cm
2.81 ft-lb/in
ASTM D256
Izod Impact, Unnotched 70.0 J/cm

@Thickness 3.20 mm
 131 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear 20.0 - 30.0 µm/m-°C

@Temperature 20.0 °C
 11.1 - 16.7 µin/in-°F

@Temperature 68.0 °F
 ASTM D696
Melting Point 260 °C
500 °F
ASTM D2133
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Arc Resistance 110 sec
110 sec
Tungsten electrode; ASTM D495
Processing Properties Metric English Comments
Processing Temperature 280 - 310 °C
536 - 590 °F
Mold Temperature 90.0 - 120 °C
194 - 248 °F