SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP AH0230A ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* AH0230A is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.30 g/cc | 0.0831 lb/in³ | ASTM D792 |
| 2.30 g/cc | 0.0831 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.160 % | 0.160 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
| 18.0 MPa | 2610 psi | ISO 527 | |
| Elongation at Break | 0.90 % | 0.90 % | ISO 527 |
| 1.4 % | 1.4 % | ASTM D638 | |
| Tensile Modulus | 5.73 GPa | 831 ksi | 50 mm/min; ASTM D638 |
| 5.89 GPa | 854 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 34.0 MPa | 4930 psi | ASTM D790 |
| 42.0 MPa | 6090 psi | ISO 178 | |
| Flexural Modulus | 5.51 GPa | 799 ksi | ASTM D790 |
| 5.54 GPa | 804 ksi | ISO 178 | |
| Izod Impact, Notched | 0.260 J/cm | 0.487 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 85.0 °C @Thickness 3.20 mm |
185 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Kinetics MIM 12 Chrome
- LG Chemical LUPOL HI5204G PP+MF20%, High Impact
- Loxim 820 02T V0 Polypropylene Compound, 20% Talc Filled, Flame Retardant
- SABIC Innovative Plastics LNP THERMOCOMP AF004 ABS (Europe-Africa-Middle East)
- Teknor Apex Telcar® TL-3954-80 Thermoplastic Elastomer
- TPI Porene® ABS-GA800 High Impact ABS Resin
- Formosa Plastics Formolene® 6375N Impact Copolymer Polypropylene
- 3M 2AU23B/UV Protective UV Tape
Copyright © lookpolymers.com All Rights Reserved