DuPont Performance Polymers Zytel® HTN FR52G30BL NC010 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN FR52G30BL NC010 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Glass Reinforced Flame Retardant PPA High Performance Polyamide Zytel HTNFR52G30BL NC010 is a 30% glass reinforced flame retardant lubricated high performance polyamide resin that has been developed for connector applications.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
DAM; ISO 1183
Viscosity Test 120 cm³/g
120 cm³/g
DAM; ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
DAM; ISO 294-4 2577
Melt Flow 26 g/10 min

@Load 2.16 kg,
Temperature 325 °C
 26 g/10 min

@Load 4.76 lb,
Temperature 617 °F
 DAM; cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
50%RH; ISO 527-1/-2
170 MPa
24700 psi
DAM; ISO 527-1/-2
Tensile Stress 18.83 MPa

@Strain 0.330 %,
Temperature 150 °C
 2731 psi

@Strain 0.330 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
20.45 MPa

@Strain 0.290 %,
Temperature 90.0 °C
 2966 psi

@Strain 0.290 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
21.71 MPa

@Strain 0.180 %,
Temperature 0.000 °C
 3149 psi

@Strain 0.180 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
22.15 MPa

@Strain 0.350 %,
Temperature 150 °C
 3213 psi

@Strain 0.350 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
22.19 MPa

@Strain 0.190 %,
Temperature 40.0 °C
 3218 psi

@Strain 0.190 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
22.3 MPa

@Strain 0.180 %,
Temperature -20.0 °C
 3230 psi

@Strain 0.180 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
22.54 MPa

@Strain 0.260 %,
Temperature 90.0 °C
 3269 psi

@Strain 0.260 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
22.73 MPa

@Strain 0.240 %,
Temperature 40.0 °C
 3297 psi

@Strain 0.240 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
22.8 MPa

@Strain 0.190 %,
Temperature 0.000 °C
 3310 psi

@Strain 0.190 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
23.63 MPa

@Strain 0.210 %,
Temperature 23.0 °C
 3427 psi

@Strain 0.210 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
25.24 MPa

@Strain 0.210 %,
Temperature -20.0 °C
 3661 psi

@Strain 0.210 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
25.57 MPa

@Strain 0.200 %,
Temperature 23.0 °C
 3709 psi

@Strain 0.200 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
52.02 MPa

@Strain 1.32 %,
Temperature 150 °C
 7545 psi

@Strain 1.32 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
60.09 MPa

@Strain 1.37 %,
Temperature 150 °C
 8715 psi

@Strain 1.37 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
62.98 MPa

@Strain 1.17 %,
Temperature 90.0 °C
 9134 psi

@Strain 1.17 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
65.3 MPa

@Strain 2.32 %,
Temperature 150 °C
 9470 psi

@Strain 2.32 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
69.2 MPa

@Strain 3.31 %,
Temperature 150 °C
 10000 psi

@Strain 3.31 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
74.6 MPa

@Strain 1.00 %,
Temperature 90.0 °C
 10800 psi

@Strain 1.00 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
75.91 MPa

@Strain 2.39 %,
Temperature 150 °C
 11010 psi

@Strain 2.39 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
78.74 MPa

@Strain 0.920 %,
Temperature 40.0 °C
 11420 psi

@Strain 0.920 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
80.8 MPa

@Strain 3.40 %,
Temperature 150 °C
 11700 psi

@Strain 3.40 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
82.4 MPa

@Strain 2.03 %,
Temperature 90.0 °C
 12000 psi

@Strain 2.03 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
82.87 MPa

@Strain 0.720 %,
Temperature 40.0 °C
 12020 psi

@Strain 0.720 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
85.18 MPa

@Strain 0.730 %,
Temperature 0.000 °C
 12350 psi

@Strain 0.730 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
87.81 MPa

@Strain 0.810 %,
Temperature 23.0 °C
 12740 psi

@Strain 0.810 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
88.7 MPa

@Strain 0.730 %,
Temperature -20.0 °C
 12900 psi

@Strain 0.730 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
88.9 MPa

@Strain 2.91 %,
Temperature 90.0 °C
 12900 psi

@Strain 2.91 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
91.67 MPa

@Strain 0.770 %,
Temperature 0.000 °C
 13300 psi

@Strain 0.770 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
91.76 MPa

@Strain 0.760 %,
Temperature 23.0 °C
 13310 psi

@Strain 0.760 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
97.54 MPa

@Strain 0.800 %,
Temperature -20.0 °C
 14150 psi

@Strain 0.800 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
104.12 MPa

@Strain 1.76 %,
Temperature 90.0 °C
 15101 psi

@Strain 1.76 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
112.47 MPa

@Strain 1.62 %,
Temperature 40.0 °C
 16312 psi

@Strain 1.62 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
118.53 MPa

@Strain 2.50 %,
Temperature 90.0 °C
 17191 psi

@Strain 2.50 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
128.53 MPa

@Strain 1.27 %,
Temperature 40.0 °C
 18642 psi

@Strain 1.27 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
129.37 MPa

@Strain 1.40 %,
Temperature 23.0 °C
 18764 psi

@Strain 1.40 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
130.1 MPa

@Strain 2.30 %,
Temperature 40.0 °C
 18870 psi

@Strain 2.30 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
132.82 MPa

@Strain 1.26 %,
Temperature 0.000 °C
 19264 psi

@Strain 1.26 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
140.43 MPa

@Strain 1.34 %,
Temperature 23.0 °C
 20368 psi

@Strain 1.34 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
141.24 MPa

@Strain 1.27 %,
Temperature -20.0 °C
 20485 psi

@Strain 1.27 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
143.2 MPa

@Strain 1.33 %,
Temperature 0.000 °C
 20770 psi

@Strain 1.33 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
153.44 MPa

@Strain 2.00 %,
Temperature 23.0 °C
 22255 psi

@Strain 2.00 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
154.25 MPa

@Strain 1.41 %,
Temperature -20.0 °C
 22372 psi

@Strain 1.41 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
157.6 MPa

@Strain 1.80 %,
Temperature 40.0 °C
 22860 psi

@Strain 1.80 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
163.4 MPa

@Strain 1.80 %,
Temperature 0.000 °C
 23700 psi

@Strain 1.80 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
165.5 MPa

@Strain 1.80 %,
Temperature 23.0 °C
 24000 psi

@Strain 1.80 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
176.85 MPa

@Strain 1.91 %,
Temperature 0.000 °C
 25650 psi

@Strain 1.91 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
177.53 MPa

@Strain 1.80 %,
Temperature -20.0 °C
 25749 psi

@Strain 1.80 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
188.54 MPa

@Strain 2.00 %,
Temperature -20.0 °C
 27345 psi

@Strain 2.00 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
Elongation at Break 2.0 %
2.0 %
DAM; ISO 527-1/-2
2.0 %
2.0 %
50%RH; ISO 527-1/-2
Tensile Modulus 11.0 GPa
1600 ksi
50%RH; ISO 527-1/-2
12.0 GPa
1740 ksi
DAM; ISO 527-1/-2
Flexural Strength 225 MPa
32600 psi
50%RH; ISO 178
250 MPa
36300 psi
DAM; ISO 178
Flexural Modulus 10.5 GPa
1520 ksi
DAM; ISO 178
Secant Modulus 6.52 GPa

@Strain 1.84 %,
Temperature 40.0 °C
 945 ksi

@Strain 1.84 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
8.5587 GPa

@Strain 0.920 %,
Temperature 40.0 °C
 1241.4 ksi

@Strain 0.920 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
8.69 GPa

@Strain 1.60 %,
Temperature 23.0 °C
 1260 ksi

@Strain 1.60 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2