DuPont Performance Polymers Zytel® FG70G30HSR3 BK309 Nylon 66 (Unverified Data**)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Zytel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® FG70G30HSR3 BK309 Nylon 66
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | |
| 1.37 g/cc | 0.0495 lb/in³ | DAM; ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | DAM; ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | DAM; ISO 294-4 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | 50%RH; ISO 527-1/-2 |
| 200 MPa | 29000 psi | DAM; ISO 527-1/-2 | |
| Elongation at Break | 3.3 % | 3.3 % | DAM; ISO 527-1/-2 |
| 5.0 % | 5.0 % | 50%RH; ISO 527-1/-2 | |
| Tensile Modulus | 7.20 GPa | 1040 ksi | 50%RH; ISO 527-1/-2 |
| 10.0 GPa | 1450 ksi | DAM; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | DAM; ISO 179/1eU |
| 9.00 J/cm² | 42.8 ft-lb/in² | 50%RH; ISO 179/1eU | |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | DAM; ISO 179/1eA |
| 1.50 J/cm² | 7.14 ft-lb/in² | 50%RH; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C | 15.6 µin/in-°F | DAM; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 95.0 µm/m-°C | 52.8 µin/in-°F | DAM; ISO 11359-1/-2 |
| Specific Heat Capacity | 2.22 J/g-°C | 0.531 BTU/lb-°F | |
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | of melt |
| Melting Point | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | DAM; ISO 75-1/-2 |
| Vicat Softening Point | 209 °C | 408 °F | DAM; 50°C/h 50N; ISO 306 |
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | DAM; 10°C/min; ISO 11357-1/-2 |
| Oxygen Index | 19 % | 19 % | DAM; ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | 50%RH; IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Delivery Form | Pellets | |
| Eff. thermal diffusivity | 6.85E-08 m²/s | |
| Processing | Injection Moulding | |
| Regional Availability | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Special Characteristics | Heat stabilised or stable to heat |
Users viewing this material also viewed the following:
- Okulen® 2000 PE-UHMW, GB
- S&E Specialty Polymers TufTech™ GA-1050 PVC Compound
- Fiberfil® PP-60/TC/13 BL8860 Polypropylene Homopolymer, 13% Talc Filled
- Ineos H03G-04 Polypropylene Homopolymer
- LATI Latamid 66 E21 G/30 PA 66, 30% Glass Fiber Reinforced
- HP Alloys Nitronic® 50 Austenitic Stainless, Level 4 Cold Worked
- Teknor Apex Monprene® MP-1890UV Thermoplastic Elastomer
- A. Schulman ComAlloy E-16769N Internally Lubricated, Glass Fiber Reinforced PPS
Copyright © lookpolymers.com All Rights Reserved