DuPont Performance Polymers Rynite® RE19051 BK507 PET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 40% Glass Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® RE19051 BK507 PET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rynite® RE19051 BK507 is a 40% glass and mineral reinforced, flame retardant, polyethylene terephthalate black resin.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.73 g/cc
0.0625 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Thickness 2.00 mm
 0.0020 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm

@Thickness 2.00 mm
 0.0090 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Index of Compound 70 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 70 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa

@Temperature 23.0 °C
 16000 psi

@Temperature 73.4 °F
 ISO 527
Elongation at Break 1.7 %

@Temperature 23.0 °C
 1.7 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 11.0 GPa

@Temperature 23.0 °C
 1600 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Strength 170 MPa

@Temperature 23.0 °C
 24700 psi

@Temperature 73.4 °F
 ISO 178
Flexural Modulus 9.70 GPa

@Temperature 23.0 °C
 1410 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.650 J/cm²

@Temperature 23.0 °C
 3.09 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 500 µm/m-°C

@Temperature -40.0 - 23.0 °C
 278 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 23.0 - 55.0 °C
 278 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
500 µm/m-°C

@Temperature 55.0 - 160 °C
 278 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
CTE, linear, Transverse to Flow 61.0 µm/m-°C

@Temperature -40.0 - 23.0 °C
 33.9 µin/in-°F

@Temperature -40.0 - 73.4 °F
 ISO 11359-1/-2
78.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 43.3 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1/-2
110 µm/m-°C

@Temperature 55.0 - 160 °C
 61.1 µin/in-°F

@Temperature 131 - 320 °F
 ISO 11359-1/-2
Melting Point 247 °C
477 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 214 °C
417 °F
ISO 75-1/-2
Glass Transition Temp, Tg 100 °C
212 °F
10°C/min; ISO 11357-1/-2
UL RTI, Electrical 155 °C

@Thickness 0.810 mm
 311 °F

@Thickness 0.0319 in
 UL 746B
UL RTI, Mechanical with Impact 155 °C

@Thickness 0.810 mm
 311 °F

@Thickness 0.0319 in
 UL 746B
UL RTI, Mechanical without Impact 155 °C

@Thickness 0.810 mm
 311 °F

@Thickness 0.0319 in
 UL 746B
Flammability, UL94 V-0

@Thickness 0.810 mm
 V-0

@Thickness 0.0319 in
 UL94
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+14 ohm-cm

@Temperature 23.0 °C
 5.00e+14 ohm-cm

@Temperature 73.4 °F
 IEC 60093
Surface Resistance >= 1.00e+15 ohm

@Temperature 23.0 °C
 >= 1.00e+15 ohm

@Temperature 73.4 °F
 IEC 60093
Dielectric Strength 32.0 kV/mm

@Temperature 23.0 °C
 813 kV/in

@Temperature 73.4 °F
 IEC 60243-1
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.020 %
<= 0.020 %
Descriptive Properties Value Comments
Drying Recommended Yes
Forms Pellets
Generic PET
Material Status Preliminary Data
Part Marking Code >PET-(MD+GF)40FR(17)<
ISO 11469
Processing Method Injection Molding
Product Category Flame Retardant Resins
Glass Reinforced Resins
Resin Identification PET-(MD+GF)40FR(17)
ISO 1043
RoHS Compliance Contact Manufacturer