Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
Manufacturer | DuPont Performance Polymers |
Trade Name | Minlon® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | DuPont Performance Polymers Minlon® 73M40 NC010 Nylon 6 (Unverified Data**).pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.28 g/cc | 0.0462 lb/in³ | |
1.45 g/cc | 0.0524 lb/in³ | DAM; ISO 1183 | |
Water Absorption | 5.4 % @Thickness 2.00 mm |
5.4 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
Moisture Absorption | 1.80 % @Thickness 2.00 mm |
1.80 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
Viscosity | 105300 cP @Shear Rate 5000 1/s, Temperature 280 °C |
105300 cP @Shear Rate 5000 1/s, Temperature 536 °F |
ISO 11403-1 -2 |
117100 cP @Shear Rate 5000 1/s, Temperature 270 °C |
117100 cP @Shear Rate 5000 1/s, Temperature 518 °F |
ISO 11403-1 -2 | |
130500 cP @Shear Rate 5000 1/s, Temperature 260 °C |
130500 cP @Shear Rate 5000 1/s, Temperature 500 °F |
ISO 11403-1 -2 | |
326200 cP @Shear Rate 500 1/s, Temperature 280 °C |
326200 cP @Shear Rate 500 1/s, Temperature 536 °F |
ISO 11403-1 -2 | |
404600 cP @Shear Rate 500 1/s, Temperature 270 °C |
404600 cP @Shear Rate 500 1/s, Temperature 518 °F |
ISO 11403-1 -2 | |
500200 cP @Shear Rate 500 1/s, Temperature 260 °C |
500200 cP @Shear Rate 500 1/s, Temperature 500 °F |
ISO 11403-1 -2 | |
Viscosity Test | 145 cm³/g | 145 cm³/g | DAM; ISO 307 1157 1628 |
Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | DAM; ISO 294-4 2577 |
Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | DAM; ISO 294-4 2577 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 59.0 MPa | 8560 psi | 50%RH; ISO 527-1/-2 |
87.0 MPa | 12600 psi | DAM; ISO 527-1/-2 | |
Tensile Stress | 7.55 MPa @Strain 0.600 %, Temperature 90.0 °C |
1100 psi @Strain 0.600 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 |
8.62 MPa @Strain 1.25 %, Temperature 150 °C |
1250 psi @Strain 1.25 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |
8.99 MPa @Strain 0.870 %, Temperature 90.0 °C |
1300 psi @Strain 0.870 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | |
20.73 MPa @Strain 0.960 %, Temperature 23.0 °C |
3007 psi @Strain 0.960 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |
23.1 MPa @Strain 8.78 %, Temperature 150 °C |
3350 psi @Strain 8.78 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |
24.23 MPa @Strain 3.51 %, Temperature 90.0 °C |
3514 psi @Strain 3.51 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | |
27.06 MPa @Strain 17.23 %, Temperature 150 °C |
3925 psi @Strain 17.23 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |
29.08 MPa @Strain 26.18 %, Temperature 150 °C |
4218 psi @Strain 26.18 %, Temperature 302 °F |
DAM; ISO 11403-1 -2 | |
30.54 MPa @Strain 6.08 %, Temperature 90.0 °C |
4429 psi @Strain 6.08 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | |
32.34 MPa @Strain 6.02 %, Temperature 90.0 °C |
4691 psi @Strain 6.02 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 | |
33.59 MPa @Strain 8.65 %, Temperature 90.0 °C |
4872 psi @Strain 8.65 %, Temperature 194 °F |
50%RH; ISO 11403-1 -2 | |
39.29 MPa @Strain 12.38 %, Temperature 90.0 °C |
5699 psi @Strain 12.38 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 | |
40.94 MPa @Strain 0.800 %, Temperature 40.0 °C |
5938 psi @Strain 0.800 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |
42.34 MPa @Strain 19.17 %, Temperature 90.0 °C |
6141 psi @Strain 19.17 %, Temperature 194 °F |
DAM; ISO 11403-1 -2 | |
42.45 MPa @Strain 3.81 %, Temperature 23.0 °C |
6157 psi @Strain 3.81 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |
50.59 MPa @Strain 0.720 %, Temperature -40.0 °C |
7337 psi @Strain 0.720 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |
52.12 MPa @Strain 6.65 %, Temperature 23.0 °C |
7559 psi @Strain 6.65 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |
56.95 MPa @Strain 9.50 %, Temperature 23.0 °C |
8260 psi @Strain 9.50 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |
61.67 MPa @Strain 18.04 %, Temperature 23.0 °C |
8944 psi @Strain 18.04 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 | |
66.28 MPa @Strain 2.93 %, Temperature 40.0 °C |
9613 psi @Strain 2.93 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |
68.33 MPa @Strain 6.04 %, Temperature 40.0 °C |
9910 psi @Strain 6.04 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |
70.17 MPa @Strain 9.22 %, Temperature 40.0 °C |
10180 psi @Strain 9.22 %, Temperature 104 °F |
DAM; ISO 11403-1 -2 | |
73.04 MPa @Strain 1.41 %, Temperature 23.0 °C |
10590 psi @Strain 1.41 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |
76.08 MPa @Strain 1.16 %, Temperature -40.0 °C |
11030 psi @Strain 1.16 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |
92.16 MPa @Strain 2.56 %, Temperature 23.0 °C |
13370 psi @Strain 2.56 %, Temperature 73.4 °F |
DAM; ISO 11403-1 -2 | |
93.81 MPa @Strain 1.80 %, Temperature 0.000 °C |
13610 psi @Strain 1.80 %, Temperature 32.0 °F |
DAM; ISO 11403-1 -2 | |
95.68 MPa @Strain 1.60 %, Temperature -40.0 °C |
13880 psi @Strain 1.60 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |
108 MPa @Strain 2.00 %, Temperature -40.0 °C |
15700 psi @Strain 2.00 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |
108.25 MPa @Strain 2.89 %, Temperature 0.000 °C |
15700 psi @Strain 2.89 %, Temperature 32.0 °F |
DAM; ISO 11403-1 -2 | |
108.64 MPa @Strain 2.02 %, Temperature -40.0 °C |
15757 psi @Strain 2.02 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |
110.15 MPa @Strain 2.08 %, Temperature -20.0 °C |
15976 psi @Strain 2.08 %, Temperature -4.00 °F |
DAM; ISO 11403-1 -2 | |
121.44 MPa @Strain 3.10 %, Temperature -20.0 °C |
17613 psi @Strain 3.10 %, Temperature -4.00 °F |
DAM; ISO 11403-1 -2 | |
122.61 MPa @Strain 2.54 %, Temperature -40.0 °C |
17783 psi @Strain 2.54 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |
124.84 MPa @Strain 3.61 %, Temperature -40.0 °C |
18107 psi @Strain 3.61 %, Temperature -40.0 °F |
50%RH; ISO 11403-1 -2 | |
133.68 MPa @Strain 3.33 %, Temperature -40.0 °C |
19389 psi @Strain 3.33 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |
138.48 MPa @Strain 4.29 %, Temperature -40.0 °C |
20085 psi @Strain 4.29 %, Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |
5.00 MPa @Strain 0.370 %, Time 3600 sec |
725 psi @Strain 0.370 %, Time 1.00 hour |
50%RH; isochronous; ISO 11403-1 -2 | |
5.00 MPa @Strain 0.430 %, Time 36000 sec |
725 psi @Strain 0.430 %, Time 10.0 hour |
50%RH; isochronous; ISO 11403-1 -2 | |
5.00 MPa @Strain 0.490 %, Time 360000 sec |
725 psi @Strain 0.490 %, Time 100 hour |
50%RH; isochronous; ISO 11403-1 -2 | |
5.00 MPa @Strain 0.600 %, Time 3.60e+6 sec |
725 psi @Strain 0.600 %, Time 1000 hour |
50%RH; isochronous; ISO 11403-1 -2 | |
Elongation at Break | 10 % | 10 % | DAM; ISO 527-1/-2 |
25 % | 25 % | 50%RH; ISO 527-1/-2 | |
Tensile Modulus | 2.20 GPa | 319 ksi | 50%RH; ISO 527-1/-2 |
6.00 GPa | 870 ksi | DAM; ISO 527-1/-2 | |
0.936 GPa @Temperature 120 °C |
136 ksi @Temperature 248 °F |
DAM; ISO 11403-1 -2 | |
4.911 GPa @Temperature 40.0 °C |
712.3 ksi @Temperature 104 °F |
DAM; ISO 11403-1 -2 | |
8.087 GPa @Temperature -40.0 °C |
1173 ksi @Temperature -40.0 °F |
DAM; ISO 11403-1 -2 | |
Flexural Modulus | 5.90 GPa | 856 ksi | DAM; ISO 178 |
Secant Modulus | 0.401 GPa @Strain 15.19 %, Temperature 23.0 °C |
58.2 ksi @Strain 15.19 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 |
0.51614 GPa @Strain 11.4 %, Temperature 23.0 °C |
74.861 ksi @Strain 11.4 %, Temperature 73.4 °F |
50%RH; ISO 11403-1 -2 |