Goodfellow Carbon/Epoxy Composite Sheet
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite |
| Manufacturer | Goodfellow |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Goodfellow Carbon/Epoxy Composite Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Carbon Fiber - Epoxy Resin MatrixInformation provided by Goodfellow.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 600 MPa | 87000 psi | Longitudinal |
| 600 MPa | 87000 psi | Transverse | |
| Elongation at Break | 0.80 % | 0.80 % | Longitudinal Compressive Strain |
| 0.80 % | 0.80 % | Transverse Compressive Strain | |
| 0.85 % | 0.85 % | Longitudinal - Tensile | |
| 0.85 % | 0.85 % | Transverse - Tensile | |
| 1.8 % | 1.8 % | Shear - In Plane | |
| Modulus of Elasticity | 70.0 GPa | 10200 ksi | Transverse |
| Tensile Modulus | 70.0 GPa | 10200 ksi | Longitudinal |
| Compressive Strength | 570 MPa | 82700 psi | Longitudinal |
| 570 MPa | 82700 psi | Transverse | |
| Shear Modulus | 5.00 GPa | 725 ksi | In Plane |
| Shear Strength | 90.0 MPa | 13100 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 2.10 µm/m-°C @Temperature 20.0 °C |
1.17 µin/in-°F @Temperature 68.0 °F |
Longitudinal |
| CTE, linear, Transverse to Flow | 2.10 µm/m-°C @Temperature 20.0 °C |
1.17 µin/in-°F @Temperature 68.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Volume Fraction Fibers, % | 50 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH GF5020 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Pyrotek Pyrocast 92AC Tabular Alumina Based Low Cement Castable
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate
- Greene Tweed CHEMRAZ® 528 Perfluoroelastomer
- Techmer ES Elastoblend® PC E IM
- UBE UBEPOL BR130B Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- Covestro Desmopan® W DP 85786A Polyurethane
- Axiall 10850 Wire & Cable Flexible PVC
- Rogers Corporation Bisco® A2 R 1.0 Engineered Solid Silicone Mass Layer, Fiberglass Reinforced Sound Barrier
- Carpenter Custom 455® Stainless Steel, Annealed, 25 mm Bar
Copyright © lookpolymers.com All Rights Reserved