DuPont Performance Polymers Hytrel® HTR8341C BK320 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® HTR8341C BK320 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
40 Shore D Lubricated High Viscosity Polyester Elastomer with Superior Fatigue Resistance Developed for Blow Molding Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
Water Absorption 0.50 %

@Thickness 2.00 mm
 0.50 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Melt Flow 0.90 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 0.90 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 37
37
15s; ISO 868
<= 40
<= 40
ISO 868
Tensile Strength at Break 28.0 MPa
4060 psi
ISO 527-1/-2
Tensile Stress 7.00 MPa

@Strain 10.0 %
 1020 psi

@Strain 10.0 %
 ISO 527-1/-2
12.0 MPa

@Strain 50.0 %
 1740 psi

@Strain 50.0 %
 ISO 527-1/-2
13.0 MPa

@Strain 100 %
 1890 psi

@Strain 100 %
 ISO 527-1/-2
23.0 MPa

@Strain 300 %
 3340 psi

@Strain 300 %
 ISO 527-1/-2
0.370 MPa

@Strain 0.160 %,
Temperature 150 °C
 53.7 psi

@Strain 0.160 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
0.390 MPa

@Strain 0.220 %,
Temperature 150 °C
 56.6 psi

@Strain 0.220 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
0.390 MPa

@Strain 0.180 %,
Temperature 120 °C
 56.6 psi

@Strain 0.180 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
0.390 MPa

@Strain 0.140 %,
Temperature 90.0 °C
 56.6 psi

@Strain 0.140 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
0.390 MPa

@Strain 0.130 %,
Temperature 60.0 °C
 56.6 psi

@Strain 0.130 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
0.410 MPa

@Strain 0.210 %,
Temperature 90.0 °C
 59.5 psi

@Strain 0.210 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
0.420 MPa

@Strain 0.250 %,
Temperature 120 °C
 60.9 psi

@Strain 0.250 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
0.420 MPa

@Strain 0.150 %,
Temperature 40.0 °C
 60.9 psi

@Strain 0.150 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
0.440 MPa

@Strain 0.120 %,
Temperature 23.0 °C
 63.8 psi

@Strain 0.120 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
0.450 MPa

@Strain 0.250 %,
Temperature 60.0 °C
 65.3 psi

@Strain 0.250 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
0.480 MPa

@Strain 0.140 %,
Temperature 0.000 °C
 69.6 psi

@Strain 0.140 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
0.510 MPa

@Strain 0.120 %,
Temperature -20.0 °C
 74.0 psi

@Strain 0.120 %,
Temperature -4.00 °F
 TPE; ISO 11403-1 -2
0.510 MPa

@Strain 0.220 %,
Temperature 23.0 °C
 74.0 psi

@Strain 0.220 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
0.570 MPa

@Strain 0.0700 %,
Temperature -40.0 °C
 82.7 psi

@Strain 0.0700 %,
Temperature -40.0 °F
 TPE; ISO 11403-1 -2
0.600 MPa

@Strain 0.250 %,
Temperature 0.000 °C
 87.0 psi

@Strain 0.250 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
0.810 MPa

@Strain 0.240 %,
Temperature -20.0 °C
 117 psi

@Strain 0.240 %,
Temperature -4.00 °F
 TPE; ISO 11403-1 -2
1.00 MPa

@Strain 0.150 %,
Temperature -40.0 °C
 145 psi

@Strain 0.150 %,
Temperature -40.0 °F
 TPE; ISO 11403-1 -2
1.26 MPa

@Strain 3.31 %,
Temperature 150 °C
 183 psi

@Strain 3.31 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
1.37 MPa

@Strain 0.230 %,
Temperature -40.0 °C
 199 psi

@Strain 0.230 %,
Temperature -40.0 °F
 TPE; ISO 11403-1 -2
1.41 MPa

@Strain 1.50 %,
Temperature 40.0 °C
 205 psi

@Strain 1.50 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
2.53 MPa

@Strain 12.19 %,
Temperature 150 °C
 367 psi

@Strain 12.19 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
2.64 MPa

@Strain 5.63 %,
Temperature 90.0 °C
 383 psi

@Strain 5.63 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
3.06 MPa

@Strain 10.48 %,
Temperature 120 °C
 444 psi

@Strain 10.48 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.17 MPa

@Strain 21.84 %,
Temperature 150 °C
 460 psi

@Strain 21.84 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
3.68 MPa

@Strain 35.38 %,
Temperature 150 °C
 534 psi

@Strain 35.38 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
4.02 MPa

@Strain 49.12 %,
Temperature 150 °C
 583 psi

@Strain 49.12 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
4.20 MPa

@Strain 22.58 %,
Temperature 120 °C
 609 psi

@Strain 22.58 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.28 MPa

@Strain 62.4 %,
Temperature 150 °C
 621 psi

@Strain 62.4 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
4.53 MPa

@Strain 75.08 %,
Temperature 150 °C
 657 psi

@Strain 75.08 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
4.77 MPa

@Strain 35.5 %,
Temperature 120 °C
 692 psi

@Strain 35.5 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.86 MPa

@Strain 92.78 %,
Temperature 150 °C
 705 psi

@Strain 92.78 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
5.05 MPa

@Strain 19.26 %,
Temperature 90.0 °C
 732 psi

@Strain 19.26 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
5.07 MPa

@Strain 103.8 %,
Temperature 150 °C
 735 psi

@Strain 103.8 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
5.25 MPa

@Strain 53.24 %,
Temperature 120 °C
 761 psi

@Strain 53.24 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.31 MPa

@Strain 116.84 %,
Temperature 150 °C
 770 psi

@Strain 116.84 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
5.62 MPa

@Strain 70.7 %,
Temperature 120 °C
 815 psi

@Strain 70.7 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.63 MPa

@Strain 133.55 %,
Temperature 150 °C
 817 psi

@Strain 133.55 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
5.63 MPa

@Strain 17.19 %,
Temperature 60.0 °C
 817 psi

@Strain 17.19 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
5.95 MPa

@Strain 87.4 %,
Temperature 120 °C
 863 psi

@Strain 87.4 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.97 MPa

@Strain 150.67 %,
Temperature 150 °C
 866 psi

@Strain 150.67 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
6.08 MPa

@Strain 33.9 %,
Temperature 90.0 °C
 882 psi

@Strain 33.9 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.27 MPa

@Strain 103.25 %,
Temperature 120 °C
 909 psi

@Strain 103.25 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.73 MPa

@Strain 125.27 %,
Temperature 120 °C
 976 psi

@Strain 125.27 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.89 MPa

@Strain 7.88 %,
Temperature 23.0 °C
 999 psi

@Strain 7.88 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
6.90 MPa

@Strain 53.74 %,
Temperature 90.0 °C
 1000 psi

@Strain 53.74 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.03 MPa

@Strain 138.82 %,
Temperature 120 °C
 1020 psi

@Strain 138.82 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.36 MPa

@Strain 37.94 %,
Temperature 60.0 °C
 1070 psi

@Strain 37.94 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
7.38 MPa

@Strain 154.66 %,
Temperature 120 °C
 1070 psi

@Strain 154.66 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.54 MPa

@Strain 73.17 %,
Temperature 90.0 °C
 1090 psi

@Strain 73.17 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.86 MPa

@Strain 174.81 %,
Temperature 120 °C
 1140 psi

@Strain 174.81 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.87 MPa

@Strain 24.3 %,
Temperature 40.0 °C
 1140 psi

@Strain 24.3 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
8.12 MPa

@Strain 91.47 %,
Temperature 90.0 °C
 1180 psi

@Strain 91.47 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.27 MPa

@Strain 59.11 %,
Temperature 60.0 °C
 1200 psi

@Strain 59.11 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
8.36 MPa

@Strain 195.3 %,
Temperature 120 °C
 1210 psi

@Strain 195.3 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2