DuPont Performance Polymers Hytrel® 6359FG NC010 TPC-ET (Unverified Data**)

Category	Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Hytrel® 6359FG NC010 TPC-ET (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Hytrel® 6359FG is a medium modulus Hytrel® grade with nominal durometer hardness of 63D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processing techniques like injection molding and extrusion. Food grade.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/in³	ISO 1183
Water Absorption	0.20 % @Temperature 23.0 °C	0.20 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62
	0.60 % @Temperature 23.0 °C	0.60 % @Temperature 73.4 °F	Saturation, immersed; ISO 62
Melt Flow	9.0 g/10 min @Load 2.16 kg, Temperature 230 °C	9.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Melt Index of Compound	8.5 g/10 min @Load 2.16 kg, Temperature 230 °C	8.5 g/10 min @Load 4.76 lb, Temperature 446 °F	cm3/10 min; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	<= 63	<= 63	ISO 868
	58 @Time 15.0 sec	58 @Time 0.00417 hour	ISO 868
Tensile Strength at Break	41.0 MPa @Temperature 23.0 °C	5950 psi @Temperature 73.4 °F	ISO 527 (1BA bar)
Tensile Stress	12.0 MPa @Strain 5.00 %, Temperature 23.0 °C	1740 psi @Strain 5.00 %, Temperature 73.4 °F	ISO 527 (1BA bar)
	15.0 MPa @Strain 10.0 %, Temperature 23.0 °C	2180 psi @Strain 10.0 %, Temperature 73.4 °F	ISO 527 (1BA bar)
Tensile Strength, Yield	19.0 MPa @Temperature 23.0 °C	2760 psi @Temperature 73.4 °F	ISO 527 (1BA bar)
Elongation at Break	>= 50 % @Temperature 23.0 °C	>= 50 % @Temperature 73.4 °F	nominal; ISO 527 (1BA bar)
	>= 300 % @Temperature 23.0 °C	>= 300 % @Temperature 73.4 °F	ISO 527 (1BA bar)
	420 % @Temperature 23.0 °C	420 % @Temperature 73.4 °F	ISO 527 (1BA bar)
Elongation at Yield	27 % @Temperature 23.0 °C	27 % @Temperature 73.4 °F	ISO 527 (1BA bar)
Tensile Modulus	0.260 GPa @Temperature 23.0 °C	37.7 ksi @Temperature 73.4 °F	ISO 527
Izod Impact, Notched (ISO)	19.0 kJ/m² @Temperature -40.0 °C	9.04 ft-lb/in² @Temperature -40.0 °F	ISO 180/1A
	81.0 kJ/m² @Temperature 23.0 °C	38.5 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact, Notched	1.50 J/cm² @Temperature -40.0 °C	7.14 ft-lb/in² @Temperature -40.0 °F	ISO 179/1eA
	2.50 J/cm² @Temperature -30.0 °C	11.9 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	12.0 J/cm² @Temperature 23.0 °C	57.1 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	211 °C	412 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	85.0 °C	185 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	45.0 °C	113 °F	ISO 75-1/-2
Brittleness Temperature	<= 100 °C	<= 212 °F	ISO 974

Processing Properties	Metric	English	Comments
Melt Temperature	230 °C	446 °F	Optimum; Extrusion
	240 °C	464 °F	Optimum; Injection Molding
Mold Temperature	45.0 °C	113 °F	optimum; Injection Molding
	45.0 - 55.0 °C	113 - 131 °F	Injection Molding
Drying Temperature	100 °C	212 °F	Extrusion
	100 °C	212 °F	Injection Molding
Dry Time	2.00 - 3.00 hour	2.00 - 3.00 hour	Extrusion
	2.00 - 3.00 hour	2.00 - 3.00 hour	Injection Molding
Moisture Content	<= 0.080 %	<= 0.080 %	Extrusion
	<= 0.080 %	<= 0.080 %	Injection Molding

Descriptive Properties	Value	Comments
Additive	Antioxidant
Appearance	Natural Color
	Natural Color
Drying Recommended	Yes
Features	Chemical Resistance
	Energy Absorption, High
	Good Creep Resistance
	Hardness, High
	Noise Dampening
Generic	TPC-ET
Material Status	Current
Part Marking Code	>TPC-ET<	ISO 11469
Processing Method	Extrusion
	Injection Molding
Product Category	Extrusion Resins
	Food Contact Resins
Region Available - Global	Yes
Resin Identification	TPC-ET	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Food Applications, Non-specific